Density

ISO 1183

g/cm^3

-

Water absorption (24h, 50%RH)

ISO 62

%

-

Deflection temperature under load (1.8MPa)

ISO 75 A

℃

-

Deflection temperature under load (0.45MPa)

ISO 75 B

℃

-

Linear expansion coefficient, flow direction (MD), -30 to 30°C

TMA

×10^-5/℃

-

Linear expansion coefficient, transverse direction (TD), -30 to 30°C

TMA

×10^-5/℃

-

Flammability (HB minimum thickness)

UL 94

mm

-

Temperature Index RTI,Elec

UL 746B

℃

-

Temperature index RTI,Imp

UL 746B

℃

-

Temperature index RTI,Str

UL 746B

℃

-

Tensile Break Strength

ISO 527

MPa

-

Tensile elongation at break

ISO 527

%

-

Tensile Modulus

ISO 527

MPa

-

Bending strength

ISO 178

MPa

-

Flexural modulus

ISO 178

MPa

-

Charpy impact strength (notched at 23℃)

ISO 179

kJ/m^2

-

Charpy impact strength (unnotched at 23℃)

ISO 179

kJ/m^2

-

Izod impact strength (notched at 23℃)

ISO 180

kJ/m^2

-

Izod impact strength (unnotched at 23℃)

ISO 180

kJ/m^2

-

Volume resistivity

IEC 6003

Ω・cm

-

Dielectric constant (1MHz)

IEC 60250

-

Dielectric tangent (1MHz)

IEC 60250

-

Withstand voltage (dielectric breakdown strength)

ASTM D149

kV/mm

-

Tracking resistance CTI

IEC 60112,Solution A

PLC level

Equivalent (UL not registered, Idemitsu Kosan Co., Ltd. Laboratory evaluation results)

Mold shrinkage, machine direction (MD)

Idemitsu Method

%

Test piece: 80 x 80 x 2 mm injection molded product

Mold shrinkage, transverse direction (TD)

Idemitsu Method

%

Test piece: 80 x 80 x 2 mm injection molded product

Cylinder Temperature

℃

-

Mold Temperature

℃

-

Drying conditions

℃

3-5 hours

Glass Fiber Content

%

-