| Manufacturer | Environmental Management Research Institute Co., Ltd. |
| Resin Name | Environmentally Friendly Resin |
| Product Name | MAPKA |
| ISO Material Code | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/JIS K7112 | Density | JIS K7112 | g/cm^3 | 1.171 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile Modulus Tensile Modulus/JIS K7113 | Tensile Modulus | JIS K7113 | MPa | 3200 | - |
Bending strength Bending strength/JIS K7203 | Bending strength | JIS K7203 | MPa | 32.5 | - |
Flexural modulus Flexural modulus/JIS K7203 | Flexural modulus | JIS K7203 | MPa | 4450 | - |
Izod impact strength Izod impact strength/JIS K7110 | IZOD Impact | JIS K7110 | kJ/m^2 | 2.5 | - |
Tensile strength Tensile strength/JIS K7113 | Tensile strength | JIS K7113 | MPa | 19 | - |
Tensile elongation Tensile elongation/JIS K7113 | Growth rate | JIS K7113 | % | 1.8 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
MFR MFR/Company method | MFR(200℃/5.0kg/10min) | Company method | g/10min | 2.8 | Measured according to our own standards |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Resin temperature Resin temperature/ | Forming temperature | ℃ | 200 | Start with a cylinder temperature of 180℃, and in case of molding short, increase the temperature by 5℃. | |
Drying conditions Drying conditions/ | Pre-drying | ℃ | 100 | 4 hours in a dehumidifying dryer or vacuum dryer. If you only have a hopper dryer, we recommend using up the pellets immediately after opening without pre-drying them. |
| Color |
|---|
White |
| Main Applications |
|---|
Paper powder (MPP) content: 51%. Hard grade of MAPKA. Suitable for products that require high bending modulus. |
| Key Features |
|---|
Paper master batch made mainly from "MPP Micro Paper Powder". Reduces CO2 emissions. Carbon neutral. National PL listed. Hard grade. |