| Manufacturer | SABIC Petrochemicals Japan |
| Resin Name | HDPE |
| Product Name | SABIC HDPE |
| ISO Material Code | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ASTM D792 | Density | ASTM D792 | g/cm^3 | 0.951 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Vicat softening temperature Vicat softening temperature/ASTM D1525 | Vicat softening point | ASTM D1525 | ℃ | 126 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile Yield Stress Tensile Yield Stress/ASTM D882 | Tensile strength, yield point, MD | ASTM D882 | MPa | 35 | - |
Tensile strength, yield point, MD | ASTM D882 | MPa | 30 | - | |
Tensile breaking stress Tensile breaking stress/ASTM D882 | Tensile strength, breaking point, MD | ASTM D882 | MPa | 50 | - |
Tensile strength, break point, TD | ASTM D882 | MPa | 48 | - | |
Tensile strain at break Tensile strain at break/ASTM D882 | Tensile elongation, break point, MD | ASTM D882 | % | 490 | - |
Tensile elongation, break point, TD | ASTM D882 | % | 500 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
MFR MFR/ASTM D1238 | Melt flow rate, 190℃/21kg | ASTM D1238 | g/10min | 8 | - |
Melt flow rate, 190℃/2.16kg | ASTM D1238 | g/10min | 0.05 | - |
| Color |
|---|
Natural |
| Main Applications |
|---|
Thin Film |
| Key Features |
|---|
Good formability, high strength, high rigidity |