| Manufacturer | Mitsubishi Chemical Corporation |
| Resin Name | PA6 |
| Product Name | PYROFIL pellet |
| ISO Material Code | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/JIS K7112 | Density | JIS K7112 | g/cm^3 | 1.27 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Bending strength Bending strength/JIS K7171 | Bending strength (1A/2) | JIS K7171 | MPa | 441 | - |
Flexural modulus Flexural modulus/JIS K7171 | Bending rigidity | JIS K7171 | MPa | 23500 | - |
Charpy impact strength Charpy impact strength/JIS K7111 | Charpy impact strength (notched) | JIS K7111 | kJ/m^2 | 11 | - |
Charpy impact strength (unnotched) | JIS K7111 | kJ/m^2 | 92 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
MVR MVR/JIS K7210 | Melt volume flow rate (300℃/2.16kg) | JIS K7210 | cm^3/10min | 40 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Resin temperature Resin temperature/ | Resin temperature | ℃ | 260 | - | |
Mold Temperature Mold Temperature/ | Mold Temperature | ℃ | 80 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Filler Content Filler Content/ | Filler Content | % | 30 | CF: Carbon fiber |
| Key Features |
|---|
High strength |