| Manufacturer | Idemitsu Kosan Co., Ltd. |
| Resin Name | PC |
| Product Name | Toughlon |
| ISO Material Code | >PC-GF15< |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ISO 1183 | Density | ISO 1183 | g/cm^3 | 1.3 | - |
Density | JIS K7112 | g/cm^3 | 1.3 | - | |
Water absorption Water absorption/ISO 62 | Water absorption (24h, 50%RH) | ISO 62 | % | 0.11 | - |
Water absorption (24h, 50%RH) | JIS K7209 | % | 0.11 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Deflection Temperature under Load Deflection Temperature under Load/ISO 75-1,2 | Deflection temperature under load (1.8MPa) | ISO 75-1,2 | ℃ | 143 | - |
Deflection temperature under load (0.45MPa) | ISO 75-1,2 | ℃ | 147 | - | |
Deflection temperature under load (1.8MPa) | JIS K7191-1,2 | ℃ | 143 | - | |
Deflection temperature under load (0.45MPa) | JIS K7191-1,2 | ℃ | 147 | - | |
Linear expansion coefficient (flow) Linear expansion coefficient (flow)/ISO 11359-2 | Linear expansion coefficient (MD) | ISO 11359-2 | ×10^-5/℃ | 3.5 | - |
Flammability Flammability/UL 94 | Flammability | UL 94 | NaN | 1.5mm |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile strain at break Tensile strain at break/ISO 527-1,2 | Tensile strain at break | ISO 527-1,2 | % | 3.5 | - |
Tensile strain at break | JIS K7161,7162 | % | 3.5 | - | |
Bending strength Bending strength/ISO 178 | Bending strength | ISO 178 | MPa | 134 | - |
Bending strength | JIS K7171 | MPa | 134 | - | |
Flexural modulus Flexural modulus/ISO 178 | Flexural modulus | ISO 178 | MPa | 4500 | - |
Flexural modulus | JIS K7171 | MPa | 4500 | - | |
Charpy impact strength Charpy impact strength/ISO179-1 | Charpy impact strength (notched, 23℃) | ISO179-1 | kJ/m^2 | 8 | Test piece thickness: 4mm |
Charpy impact strength (notched, 23℃) | JIS K7111 | kJ/m^2 | 8 | Test piece thickness: 4mm | |
Surface hardness Surface hardness/ISO 2039-2 | Rockwell hardness | ISO 2039-2 | R scale | 120 | - |
Rockwell hardness | ISO 2039-2 | M scale | 73 | - | |
Rockwell hardness | JIS K7202-2 | R scale | 120 | - | |
Rockwell hardness | JIS K7202-2 | M scale | 73 | - | |
Tensile strength Tensile strength/ISO 527-1,2 | Tensile (yield) strength | ISO 527-1,2 | MPa | 87 | - |
Tensile (yield) strength | JIS K7161,7162 | MPa | 87 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/Idemitsu Method | Mold shrinkage rate (2mm,MD) | Idemitsu Method | % | 0.3 | - |
Mold shrinkage rate TD Mold shrinkage rate TD/Idemitsu Method | Mold shrinkage rate (2mm,TD) | Idemitsu Method | % | 0.6 | - |
MVR MVR/ISO 1133 | Melt volume flow rate (MVR, 300℃, 1.20kg) | ISO 1133 | cm^3/10min | 2.3 | - |
Melt volume flow rate (MVR, 300℃, 1.20kg) | JIS K7210 | cm^3/10min | 2.3 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Resin temperature Resin temperature/ | Cylinder Temperature | % | Upper limit 320℃ | ||
Mold Temperature Mold Temperature/ | Mold Temperature | ℃ | - | ||
Drying conditions Drying conditions/ | Drying conditions | ℃ | 120 | 5~8 hours |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Filler Content Filler Content/ | Filler Content | % | 15 | GF |
| Key Features |
|---|
Glass fiber reinforced grade/Flame retardant V-2 |