| Manufacturer | Lotte Chemical Japan Co., Ltd. |
| Resin Name | PC |
| Product Name | INFINO |
| ISO Material Code | PC |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ISO 1183 | Proportion | ISO 1183 | 1.18 | - | |
Proportion | ASTM D792 | 1.18 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Vicat softening temperature Vicat softening temperature/ISO 306 | Vicat softening temperature (B/50) | ISO 306 | ℃ | 98 | - |
Vicat softening temperature (B/120) | ISO 306 | ℃ | 100 | - | |
Deflection Temperature under Load Deflection Temperature under Load/ISO 75-2 | Heat distortion temperature (without annealing) (1.80MPa, 4.0mm) | ISO 75-2 | ℃ | 81 | - |
Heat distortion temperature (without annealing) (0.45MPa, 4.0mm) | ISO 75-2 | ℃ | 93 | - | |
Heat distortion temperature (annealed) (1.80MPa, 4.0mm) | ISO 75-2 | ℃ | 93 | - | |
Heat distortion temperature (annealed) (0.45MPa, 4.0mm) | ISO 75-2 | ℃ | 98 | - | |
Flammability Flammability/UL 94 | Flammability | UL 94 | NaN | 1.2mm/1.3mm | |
Flammability | UL 94 | NaN | 1.5mm/2.0mm/2.1mm/2.5mm/3.0mm | ||
Flammability | UL 94 | NaN | 3.0mm | ||
Flammability | UL 94 | NaN | 2.0mm/2.1mm/2.5mm |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile Yield Stress Tensile Yield Stress/ISO 527 | Tensile strength (yield point), 50mm/min | ISO 527 | MPa | 60 | - |
Tensile strength (yield point), 50mm/min | ASTM D638 | MPa | 61.78 | - | |
Tensile breaking stress Tensile breaking stress/ISO 527 | Tensile strength (break point), 50mm/min | ISO 527 | MPa | 48 | - |
Tensile Modulus Tensile Modulus/ISO 527 | Tensile modulus, 50mm/min | ISO 527 | MPa | 2500 | - |
Bending strength Bending strength/ISO 178 | Bending strength, 2mm/min | ISO 178 | MPa | 88 | - |
Bending strength, 2.8mm/min | ASTM D790 | MPa | 86.3 | - | |
Flexural modulus Flexural modulus/ISO 178 | Flexural modulus, 2mm/min | ISO 178 | MPa | 2450 | - |
Flexural modulus: 2.8mm/min | ASTM D790 | MPa | 2255.53 | - | |
Charpy impact strength Charpy impact strength/ISO 179 1eA | Charpy impact strength (with V notch), 23℃, 4mm | ISO 179 1eA | kJ/m^2 | 44 | - |
Izod impact strength Izod impact strength/ISO 180 1A | Izod impact strength (notched), 23℃, 4mm | ISO 180 1A | kJ/m^2 | 40 | - |
Izod impact strength (notched), 1/8 inch, 23℃ | ASTM D256 | J/m | 558.6 | - | |
Surface hardness Surface hardness/ISO 2039-2 | Rockwell Hardness | ISO 2039-2 | R scale | 118 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tracking resistance Tracking resistance/UL 746A | Hot Wire Ignition (1.5) | UL 746A | PLC | 2 | - |
High Current Arc Ignition (1.5) | UL 746A | PLC | 3 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/ISO 294-4 | Mold shrinkage (MD), Flow at 2mm | ISO 294-4 | % | - | |
Mold shrinkage (MD), Flow at 3.2mm | ASTM D955 | % | - | ||
Mold shrinkage rate TD Mold shrinkage rate TD/ISO 294-4 | Mold shrinkage (TD), X-Flow at 2mm | ISO 294-4 | % | - | |
Mold shrinkage (TD), X-Flow at 3.2mm | ASTM D955 | % | - | ||
MFR MFR/ISO 1133 | Melt mass flow rate (220℃, 10kg) | ISO 1133 | g/10min | 23 | - |
Melt mass flow rate (220℃, 10kg) | ASTM D1238 | g/10min | 23 | - |
| Key Features |
|---|
High Impact |