| Manufacturer | Lotte Chemical Japan Co., Ltd. |
| Resin Name | PC |
| Product Name | INFINO |
| ISO Material Code | PC |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ISO 1183 | Proportion | ISO 1183 | 1.33 | - | |
Proportion | ASTM D792 | 1.33 | - | ||
Water absorption Water absorption/ISO 62 | Water absorption (23℃) | ISO 62 | % | 0.15 | - |
Water absorption (23℃) | ASTM D570 | % | 0.15 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Deflection Temperature under Load Deflection Temperature under Load/ISO 75-2 | Heat distortion temperature (without annealing) (1.80MPa, 4.0mm) | ISO 75-2 | ℃ | 137 | - |
Heat distortion temperature (without annealing) (0.45MPa, 4.0mm) | ISO 75-2 | ℃ | 142 | - | |
Heat distortion temperature (18.56kgf/cm^2, 6.4mm) | ASTM D648 | ℃ | 139 | - | |
Heat distortion temperature (4.6kgf/cm^2, 6.4mm) | ASTM D648 | ℃ | 143 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile breaking stress Tensile breaking stress/ISO 527 | Tensile strength (break point), 5mm/min | ISO 527 | MPa | 100 | - |
Tensile strength (break point), 5mm/min | ASTM D638 | MPa | 98.07 | - | |
Tensile strain at break Tensile strain at break/ISO 527 | Tensile strain (break point), 5mm/min | ISO 527 | % | 4 | - |
Tensile strain (break point), 5mm/min | ASTM D638 | % | 4 | - | |
Tensile Modulus Tensile Modulus/ISO 527 | Tensile modulus, 5mm/min | ISO 527 | MPa | 5700 | - |
Tensile modulus, 5mm/min | ASTM D638 | MPa | 5295.59 | - | |
Bending strength Bending strength/ISO 178 | Bending strength, 2mm/min | ISO 178 | MPa | 170 | - |
Bending strength, 2.8mm/min | ASTM D790 | MPa | 137.29 | - | |
Flexural modulus Flexural modulus/ISO 178 | Flexural modulus, 2mm/min | ISO 178 | MPa | 6000 | - |
Flexural modulus: 2.8mm/min | ASTM D790 | MPa | 5491.72 | - | |
Charpy impact strength Charpy impact strength/ISO 179 1eA | Charpy impact strength (with V notch), 23℃, 4mm | ISO 179 1eA | kJ/m^2 | 25 | - |
Izod impact strength Izod impact strength/ISO 180 1A | Izod impact strength (notched), 23℃, 4mm | ISO 180 1A | kJ/m^2 | 19 | - |
Izod impact strength (notched), 1/4 inch, 23℃ | ASTM D256 | J/m | 176.4 | - | |
Izod impact strength (notched), 1/8 inch, 23℃ | ASTM D256 | J/m | 186.2 | - | |
Surface hardness Surface hardness/ISO 2039-2 | Rockwell Hardness | ISO 2039-2 | R scale | 116 | - |
Rockwell Hardness | ASTM D785 | R scale | 116 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/ISO 294-4 | Mold shrinkage (MD), Flow at 2mm | ISO 294-4 | % | - | |
Mold shrinkage (MD), Flow at 3.2mm | ASTM D955 | % | - | ||
Mold shrinkage rate TD Mold shrinkage rate TD/ISO 294-4 | Mold shrinkage (TD), X-Flow at 2mm | ISO 294-4 | % | - | |
Mold shrinkage (TD), X-Flow at 3.2mm | ASTM D955 | % | - | ||
MFR MFR/ISO 1133 | Melt mass flow rate (250℃, 10kg) | ISO 1133 | g/10min | 23 | - |
Melt mass flow rate (250℃, 10kg) | ASTM D1238 | g/10min | 23 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Filler Content Filler Content/ | Filler Content | % | 20 | GF |
| Main Applications |
|---|
Mobile phone |
| Key Features |
|---|
Environmentally friendly (30% recycled PC) |