| Manufacturer | Lotte Chemical Japan Co., Ltd. |
| Resin Name | PC |
| Product Name | INFINO |
| ISO Material Code | PC |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ISO 1183 | Proportion | ISO 1183 | 1.16 | - | |
Proportion | ASTM D792 | 1.16 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Vicat softening temperature Vicat softening temperature/ISO 306 | Vicat softening temperature (B/50) | ISO 306 | ℃ | 139 | - |
Deflection Temperature under Load Deflection Temperature under Load/ISO 75-2 | Heat distortion temperature (without annealing) (1.80MPa, 4.0mm) | ISO 75-2 | ℃ | 113 | - |
Heat distortion temperature (without annealing) (0.45MPa, 4.0mm) | ISO 75-2 | ℃ | 133 | - | |
Heat distortion temperature (18.56kgf/cm^2, 6.4mm) | ASTM D648 | ℃ | 115 | - | |
Linear expansion coefficient (flow) Linear expansion coefficient (flow)/ISO 11359-1/-2 | Linear expansion coefficient (flow 40-100℃) | ISO 11359-1/-2 | ×10^-5/℃ | 7.2 | - |
Linear expansion coefficient (flow 40-100℃) | ASTM E831 | ×10^-5/℃ | 7.2 | - | |
Linear expansion coefficient (right angle) Linear expansion coefficient (right angle)/ISO 11359-1/-2 | Linear expansion coefficient (X-Flow 40 to 100°C) | ISO 11359-1/-2 | ×10^-5/℃ | 7.8 | - |
Linear expansion coefficient (X-Flow 40 to 100°C) | ASTM E831 | ×10^-5/℃ | 7.8 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile Yield Stress Tensile Yield Stress/ISO 527 | Tensile strength (yield point), 50mm/min | ISO 527 | MPa | 60 | - |
Tensile strength (yield point), 50mm/min | ASTM D638 | MPa | 58.84 | - | |
Tensile breaking stress Tensile breaking stress/ISO 527 | Tensile strength (break point), 50mm/min | ISO 527 | MPa | 55 | - |
Tensile strength (break point), 50mm/min | ASTM D638 | MPa | 55.9 | - | |
Tensile strain at break Tensile strain at break/ISO 527 | Tensile strain (break point), 50mm/min | ISO 527 | % | 100 | - |
Tensile strain (break point), 50mm/min | ASTM D638 | % | 100 | - | |
Tensile Modulus Tensile Modulus/ISO 527 | Tensile modulus, 50mm/min | ISO 527 | MPa | 2350 | - |
Tensile modulus, 50mm/min | ASTM D638 | MPa | 2157.46 | - | |
Bending strength Bending strength/ISO 178 | Bending strength, 2mm/min | ISO 178 | MPa | 90 | - |
Bending strength, 2.8mm/min | ASTM D790 | MPa | 83.36 | - | |
Flexural modulus Flexural modulus/ISO 178 | Flexural modulus, 2mm/min | ISO 178 | MPa | 2400 | - |
Flexural modulus: 2.8mm/min | ASTM D790 | MPa | 2206.5 | - | |
Charpy impact strength Charpy impact strength/ISO 179 1eA | Charpy impact strength (with V notch), 23℃, 4mm | ISO 179 1eA | kJ/m^2 | 60 | - |
Izod impact strength Izod impact strength/ISO 180 1A | Izod impact strength (notched), 23℃, 4mm | ISO 180 1A | kJ/m^2 | 50 | - |
Izod impact strength (notched), -30℃, 4mm | ISO 180 1A | kJ/m^2 | 18 | - | |
Izod impact strength (notched), 1/4 inch, 23℃ | ASTM D256 | J/m | 441 | - | |
Izod impact strength (notched), 1/8 inch, 23℃ | ASTM D256 | J/m | 686 | - | |
Izod impact strength (notched), 1/4 inch, -30℃ | ASTM D256 | J/m | 98 | - | |
Izod impact strength (notched), 1/8 inch, -30℃ | ASTM D256 | J/m | 176.4 | - | |
Surface hardness Surface hardness/ISO 2039-2 | Rockwell Hardness | ISO 2039-2 | R scale | 110 | - |
Rockwell Hardness | ASTM D785 | R scale | 110 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/ASTM D955 | Mold shrinkage (MD), Flow at 3.2mm | ASTM D955 | % | - | |
Mold shrinkage rate TD Mold shrinkage rate TD/ASTM D955 | Mold shrinkage (TD), X-Flow at 3.2mm | ASTM D955 | % | - | |
MFR MFR/ISO 1133 | Melt mass flow rate (250℃, 10kg) | ISO 1133 | g/10min | 38 | - |
Melt mass flow rate (250℃, 10kg) | ASTM D1238 | g/10min | 38 | - |
| Main Applications |
|---|
Front grill, body panel |
| Key Features |
|---|
Ultra high heat resistance |