Density (dry)

ISO 1183

g/cm^3

-

Equilibrium water absorption (2mm) (when absorbing moisture)

ISO 62

%

-

Water absorption (immersion, 24h) (when completely dry)

ISO 62

%

-

Vicat softening temperature (50℃/h 50N) (when completely dry)

ISO 306

℃

-

Deflection temperature under load (1.80 MPa) (when completely dry)

ISO 75-1/-2

℃

-

Deflection temperature under load (0.45 MPa) (when completely dry)

ISO 75-1/-2

℃

-

Melting temperature (10℃/min) (when completely dry)

ISO 11357-1/-3

℃

-

Flammability

IEC 60695-11-10

class

1.5ｍｍ

Breaking stress (when completely dry)

ISO 527-1/-2

MPa

-

Breaking stress (at 23℃ 50% RH equilibrium water absorption)

ISO 527-1/-2

MPa

-

Breaking strain (when completely dry)

ISO 527-1/-2

%

-

Breaking strain (at 23℃ 50% RH equilibrium water absorption)

ISO 527-1/-2

%

-

Tensile modulus (when completely dry)

ISO 527-1/-2

MPa

-

Tensile modulus (at 23℃ 50% RH equilibrium water absorption)

ISO 527-1/-2

MPa

-

Notched Charpy impact strength (23°C) (when completely dry)

ISO 179/1eA

kJ/m^2

-

Notched Charpy impact strength (23℃) (23℃ 50%RH equilibrium water absorption)

ISO 179/1eA

kJ/m^2

-

Notched Charpy impact strength (-30℃) (absolutely dry)

ISO 179/1eA

kJ/m^2

-

Notched Charpy impact strength (-30℃) (23℃ 50%RH equilibrium water absorption)

ISO 179/1eA

kJ/m^2

-

Charpy impact strength (23℃) (when completely dry)

ISO 179/1eU

kJ/m^2

-

Charpy impact strength (23℃) (23℃ 50% RH equilibrium water absorption)

ISO 179/1eU

kJ/m^2

-

Charpy impact strength (-30℃) (when completely dry)

ISO 179/1eU

kJ/m^2

-

Charpy impact strength (-30℃) (23℃ 50% RH equilibrium water absorption)

ISO 179/1eU

kJ/m^2

-

Mold shrinkage rate (parallel) (when completely dry)

ISO 294-4,2577

%

-

Mold shrinkage rate (vertical) (when completely dry)

ISO 294-4,2577

%

-

Optimum resin temperature

℃

-

Optimal Mold Temperature

℃

-

Drying temperature

℃

2 - 4h

Filler Content

%

GF