Density (dry)

ISO 1183

g/cm^3

-

Equilibrium water absorption (2mm) (when absorbing moisture)

ISO 62

%

-

Deflection temperature under load (1.80 MPa) (when completely dry)

ISO 75-1/-2

℃

-

Deflection temperature under load (0.45 MPa) (when completely dry)

ISO 75-1/-2

℃

-

Linear expansion coefficient (parallel) (when completely dry)

ISO 11359-1/-2

x10^-5/℃

-

Linear expansion coefficient (right angle) (when completely dry)

ISO 11359-1/-2

x10^-5/℃

-

Melting temperature (10℃/min) (when completely dry)

ISO 11357-1/-3

℃

-

Flammability

IEC 60695-11-10

class

1.5ｍｍ

Yield stress (absolutely dry)

ISO 527-1/-2

MPa

-

Yield stress (at 23℃ 50% RH equilibrium water absorption)

ISO 527-1/-2

MPa

-

Tensile modulus (when completely dry)

ISO 527-1/-2

MPa

-

Tensile modulus (at 23℃ 50% RH equilibrium water absorption)

ISO 527-1/-2

MPa

-

Notched Charpy impact strength (23°C) (when completely dry)

ISO 179/1eA

kJ/m^2

-

Notched Charpy impact strength (-30℃) (absolutely dry)

ISO 179/1eA

kJ/m^2

-

Notched Charpy impact strength (-40℃) (absolutely dry)

ISO 179/1eA

kJ/m^2

-

Charpy impact strength (23℃) (when completely dry)

ISO 179/1eU

kJ/m^2

-

Yield strain (when completely dry)

ISO 527-1/-2

%

-

Yield strain (at 23℃ 50% RH equilibrium water absorption)

ISO 527-1/-2

%

-

Mold shrinkage rate (parallel) (when completely dry)

ISO 294-4,2577

%

-

Mold shrinkage rate (vertical) (when completely dry)

ISO 294-4,2577

%

-

Melt mass flow rate (275℃, 10kg) (absolutely dry)

ISO 1133

g/10min

-

Optimum resin temperature

℃

-

Optimal Mold Temperature

℃

-

Drying temperature

℃

2 - 4h

Filler Content

%

GF