| Manufacturer | Celanese Corporation |
| Resin Name | PA66 |
| Product Name | Zytel |
| ISO Material Code | PA66+PA6-IGF18 |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ISO 1183 | Density (dry) | ISO 1183 | g/cm^3 | 1.22 | - |
Water absorption Water absorption/ISO 62 | Equilibrium water absorption (2mm) (when absorbing moisture) | ISO 62 | % | 2.2 | - |
Water absorption (immersion, 24h) (when completely dry) | ISO 62 | % | 3.2 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Deflection Temperature under Load Deflection Temperature under Load/ISO 75-1/-2 | Deflection temperature under load (1.80 MPa) (when completely dry) | ISO 75-1/-2 | ℃ | 195 | - |
Deflection temperature under load (0.45 MPa) (when completely dry) | ISO 75-1/-2 | ℃ | 235 | - | |
Melting point Melting point/ISO 11357-1/-3 | Melting temperature (10℃/min) (when completely dry) | ISO 11357-1/-3 | ℃ | 245 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile Yield Stress Tensile Yield Stress/ISO 527-1/-2 | Yield stress (absolutely dry) | ISO 527-1/-2 | MPa | 100 | - |
Yield stress (at 23℃ 50% RH equilibrium water absorption) | ISO 527-1/-2 | MPa | 50 | - | |
Tensile strain at break Tensile strain at break/ISO 527-1/-2 | Breaking strain (when completely dry) | ISO 527-1/-2 | % | 4 | - |
Breaking strain (at 23℃ 50% RH equilibrium water absorption) | ISO 527-1/-2 | % | 28 | - | |
Tensile Modulus Tensile Modulus/ISO 527-1/-2 | Tensile modulus (when completely dry) | ISO 527-1/-2 | MPa | 5400 | - |
Tensile modulus (at 23℃ 50% RH equilibrium water absorption) | ISO 527-1/-2 | MPa | 2600 | - | |
Bending strength Bending strength/ISO 178 | Bending strength (when completely dry) | ISO 178 | MPa | 145 | - |
Bending strength (at 23℃ 50% RH equilibrium water absorption) | ISO 178 | MPa | 5 | - | |
Flexural modulus Flexural modulus/ISO 178 | Flexural modulus (when completely dry) | ISO 178 | MPa | 4900 | - |
Flexural modulus (at 23℃ 50% RH equilibrium water absorption) | ISO 178 | MPa | 2300 | - | |
Charpy impact strength Charpy impact strength/ISO 179/1eA | Notched Charpy impact strength (23°C) (when completely dry) | ISO 179/1eA | kJ/m^2 | 13 | - |
Notched Charpy impact strength (23℃) (23℃ 50%RH equilibrium water absorption) | ISO 179/1eA | kJ/m^2 | 22 | - | |
Notched Charpy impact strength (-30℃) (absolutely dry) | ISO 179/1eA | kJ/m^2 | 6 | - | |
Notched Charpy impact strength (-30℃) (23℃ 50%RH equilibrium water absorption) | ISO 179/1eA | kJ/m^2 | 5 | - | |
Notched Charpy impact strength (-40℃) (absolutely dry) | ISO 179/1eA | kJ/m^2 | 5 | - | |
Notched Charpy impact strength (-40℃) (23℃ 50%RH equilibrium water absorption) | ISO 179/1eA | kJ/m^2 | 3.5 | - | |
Charpy impact strength (23℃) (when completely dry) | ISO 179/1eU | kJ/m^2 | 68 | - | |
Charpy impact strength (23℃) (23℃ 50% RH equilibrium water absorption) | ISO 179/1eU | kJ/m^2 | 100 | - | |
Charpy impact strength (-30℃) (when completely dry) | ISO 179/1eU | kJ/m^2 | 65 | - | |
Charpy impact strength (-30℃) (23℃ 50% RH equilibrium water absorption) | ISO 179/1eU | kJ/m^2 | 90 | - | |
Izod impact strength Izod impact strength/ISO 179/1eU | Izod impact strength, unnotched (-40°C) (when completely dry) | ISO 179/1eU | kJ/m^2 | 65 | - |
Izod impact strength, unnotched (-40℃) (at 23℃ 50% RH equilibrium water absorption) | ISO 179/1eU | kJ/m^2 | 45 | - | |
Yield Strain Yield Strain/ISO 527-1/-2 | Yield strain (when completely dry) | ISO 527-1/-2 | % | 3 | - |
Yield strain (at 23℃ 50% RH equilibrium water absorption) | ISO 527-1/-2 | % | 10 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/ISO 294-4,2577 | Mold shrinkage rate (parallel) (when completely dry) | ISO 294-4,2577 | % | 0.8 | - |
Mold shrinkage rate TD Mold shrinkage rate TD/ISO 294-4,2577 | Mold shrinkage rate (vertical) (when completely dry) | ISO 294-4,2577 | % | 0.6 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Resin temperature Resin temperature/ | Optimum resin temperature | ℃ | 290 | - | |
Mold Temperature Mold Temperature/ | Optimal Mold Temperature | ℃ | 90 | - | |
Drying conditions Drying conditions/ | Drying temperature | ℃ | 80 | 2 - 4h |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Filler Content Filler Content/ | Filler Content | % | 18 | GF |