| Manufacturer | Celanese Corporation |
| Resin Name | PA66 |
| Product Name | Zytel |
| ISO Material Code | PA66-GF30 |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ISO 1183 | Density (dry) | ISO 1183 | g/cm^3 | 1.37 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Deflection Temperature under Load Deflection Temperature under Load/ISO 75-1/-2 | Deflection temperature under load (1.80 MPa) (when completely dry) | ISO 75-1/-2 | ℃ | 248 | - |
Deflection temperature under load (0.45 MPa) (when completely dry) | ISO 75-1/-2 | ℃ | 260 | - | |
Melting point Melting point/ISO 11357-1/-3 | Melting temperature (10℃/min) (when completely dry) | ISO 11357-1/-3 | ℃ | 263 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile breaking stress Tensile breaking stress/ISO 527-1/-2 | Breaking stress (when completely dry) | ISO 527-1/-2 | MPa | 192 | - |
Breaking stress (at 23℃ 50% RH equilibrium water absorption) | ISO 527-1/-2 | MPa | 130 | - | |
Tensile strain at break Tensile strain at break/ISO 527-1/-2 | Breaking strain (when completely dry) | ISO 527-1/-2 | % | 3.2 | - |
Breaking strain (at 23℃ 50% RH equilibrium water absorption) | ISO 527-1/-2 | % | 4.5 | - | |
Tensile Modulus Tensile Modulus/ISO 527-1/-2 | Tensile modulus (when completely dry) | ISO 527-1/-2 | MPa | 10000 | - |
Tensile modulus (at 23℃ 50% RH equilibrium water absorption) | ISO 527-1/-2 | MPa | 7200 | - | |
Bending strength Bending strength/ISO 178 | Bending strength (when completely dry) | ISO 178 | MPa | 280 | - |
Bending strength (at 23℃ 50% RH equilibrium water absorption) | ISO 178 | MPa | 190 | - | |
Flexural modulus Flexural modulus/ISO 178 | Flexural modulus (when completely dry) | ISO 178 | MPa | 8500 | - |
Flexural modulus (at 23℃ 50% RH equilibrium water absorption) | ISO 178 | MPa | 6000 | - | |
Charpy impact strength Charpy impact strength/ISO 179/1eA | Notched Charpy impact strength (23°C) (when completely dry) | ISO 179/1eA | kJ/m^2 | 11 | - |
Notched Charpy impact strength (23℃) (23℃ 50%RH equilibrium water absorption) | ISO 179/1eA | kJ/m^2 | 15 | - | |
Notched Charpy impact strength (-40℃) (absolutely dry) | ISO 179/1eA | kJ/m^2 | 9 | - | |
Notched Charpy impact strength (-40℃) (23℃ 50%RH equilibrium water absorption) | ISO 179/1eA | kJ/m^2 | 10 | - | |
Charpy impact strength (23℃) (when completely dry) | ISO 179/1eU | kJ/m^2 | 70 | - | |
Charpy impact strength (23℃) (23℃ 50% RH equilibrium water absorption) | ISO 179/1eU | kJ/m^2 | 90 | - | |
Izod impact strength Izod impact strength/ISO 180/1A | Izod impact strength, notched (23°C) (when completely dry) | ISO 180/1A | kJ/m^2 | 11 | - |
Izod impact strength, notched (23°C) (at 23°C, 50% RH, equilibrium water absorption) | ISO 180/1A | kJ/m^2 | 15 | - | |
Izod impact strength, notched (-40°C) (absolutely dry) | ISO 180/1A | kJ/m^2 | 9 | - | |
Izod impact strength, notched (-40℃) (23℃ 50% RH equilibrium water absorption) | ISO 180/1A | kJ/m^2 | - | ||
Izod impact strength, unnotched (23°C) (when completely dry) | ISO 180/1U | kJ/m^2 | 70 | - | |
Izod impact strength, unnotched (23°C) (at 23°C and 50% RH when absorbing water at equilibrium) | ISO 180/1U | kJ/m^2 | 80 | - | |
Izod impact strength, unnotched (-40°C) (when completely dry) | ISO 179/1eU | kJ/m^2 | 60 | - | |
Izod impact strength, unnotched (-40℃) (at 23℃ 50% RH equilibrium water absorption) | ISO 179/1eU | kJ/m^2 | 50 | - | |
Izod impact strength, unnotched (-40°C) (when completely dry) | ISO 179/1eU | kJ/m^2 | 65 | - | |
Izod impact strength, unnotched (-40℃) (at 23℃ 50% RH equilibrium water absorption) | ISO 179/1eU | kJ/m^2 | 60 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/ISO 294-4,2577 | Mold shrinkage rate (parallel) (when completely dry) | ISO 294-4,2577 | % | 0.3 | - |
Mold shrinkage rate TD Mold shrinkage rate TD/ISO 294-4,2577 | Mold shrinkage rate (vertical) (when completely dry) | ISO 294-4,2577 | % | 1 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Resin temperature Resin temperature/ | Optimum resin temperature | ℃ | 295 | - | |
Mold Temperature Mold Temperature/ | Optimal Mold Temperature | ℃ | 100 | - | |
Drying conditions Drying conditions/ | Drying temperature | ℃ | 80 | 2 - 4h |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Filler Content Filler Content/ | Filler Content | % | 30 | GF |