| Manufacturer | Mitsubishi Chemical Corporation |
| Resin Name | PBT |
| Product Name | NOVADURAN |
| ISO Material Code | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ISO 1183 | Density | ISO 1183 | g/cm^3 | 1.38 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Deflection Temperature under Load Deflection Temperature under Load/ISO 75-1,2 | Deflection temperature under load (1.80MPa) | ISO 75-1,2 | ℃ | 195 | - |
Deflection temperature under load (0.45MPa) | ISO 72-1,2 | ℃ | 200 | - | |
Linear expansion coefficient (flow) Linear expansion coefficient (flow)/ISO 11359-2 | Linear expansion coefficient (MD: -30 to 120°C) | ISO 11359-2 | ×10^-5/℃ | 3 | - |
Linear expansion coefficient (MD: -30 to 35°C) | ISO 11359-2 | ×10^-5/℃ | 4.2 | - | |
Linear expansion coefficient (MD: 35 to 120°C) | ISO 11359-2 | ×10^-5/℃ | 2.1 | - | |
Linear expansion coefficient (right angle) Linear expansion coefficient (right angle)/ISO 11359-2 | Linear expansion coefficient (TD: -30 to 120°C) | ISO 11359-2 | ×10^-5/℃ | 15 | - |
Linear expansion coefficient (TD: -30 to 35°C) | ISO 11359-2 | ×10^-5/℃ | 10.6 | - | |
Linear expansion coefficient (TD: 35 to 120°C) | ISO 11359-1 | ×10^-5/℃ | 18.3 | - | |
Melting point Melting point/ISO 11357-3 | Melting Temperature | ISO 11357-3 | ℃ | 224 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile breaking stress Tensile breaking stress/ISO 527-1,2 | Breaking Stress | ISO 527-1,2 | MPa | 90 | - |
Tensile strain at break Tensile strain at break/ISO 527-1,2 | Destructive strain | ISO 527-1,2 | % | 3 | - |
Bending strength Bending strength/ISO 178 | Bending strength | ISO 178 | MPa | 145 | - |
Flexural modulus Flexural modulus/ISO 178 | Flexural modulus | ISO 178 | MPa | 4700 | - |
Charpy impact strength Charpy impact strength/ISO 179-1,2 | Charpy impact (unnotched) | ISO 179-1,2 | kJ/m^2 | 29 | - |
Charpy impact (with notch) | ISO 179-1,2 | kJ/m^2 | 7 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/- | Mold shrinkage rate MD(2mmt) | - | % | 0.5 | - |
Mold shrinkage rate TD Mold shrinkage rate TD/- | Mold shrinkage TD (2mmt) | - | % | 1.3 | - |
MVR MVR/ISO 1133 | Melt volume flow rate (250℃×5kg) | ISO 1133 | cm^3/10min | 100 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Resin temperature Resin temperature/- | Forming temperature | - | ℃ | - | |
Mold Temperature Mold Temperature/- | Mold Temperature | - | ℃ | - | |
Drying conditions Drying conditions/- | Drying temperature | - | ℃ | 120 | 5-8h |
Drying temperature | - | ℃ | 140 | 4-6h |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Filler Content Filler Content/ | Filler Content | % | 15 | GF |
| Key Features |
|---|
Super resistant to hydrolysis |