| Manufacturer | Mitsubishi Chemical Corporation |
| Resin Name | PC FR |
| Product Name | XANTAR |
| ISO Material Code | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ISO 1183 | Density | ISO 1183 | g/cm3 | 1.26 | - |
Water absorption Water absorption/Sim. to ISO 62 | Sim. to ISO 62 | % | 0.35 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Vicat softening temperature Vicat softening temperature/ISO 306 | Vicat softening temperature (50℃/h 50N) | ISO 306 | ℃ | 145 | - |
Deflection Temperature under Load Deflection Temperature under Load/ISO 75-1/-2 | Deflection temperature under load (1.8MPa) | ISO 75-1/-2 | ℃ | 126 | - |
Flammability Flammability/IEC 60695-11-10 | Flammability at thickness h | IEC 60695-11-10 | class | NaN | 0.75mm |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile Yield Stress Tensile Yield Stress/ISO 527-1/-2 | Yield Stress | ISO 527-1/-2 | MPa | 60 | - |
Tensile strain at break Tensile strain at break/ISO 527-1/-2 | Nominal breaking strain | ISO 527-1/-2 | % | 50 | - |
Tensile Modulus Tensile Modulus/ISO 527-1/-2 | Tensile Modulus | ISO 527-1/-2 | MPa | 2300 | - |
Bending strength Bending strength/ISO 178 | Bending strength | ISO 178 | MPa | 90 | - |
Flexural modulus Flexural modulus/ISO 178 | Flexural modulus | ISO 178 | MPa | 2400 | - |
Izod impact strength Izod impact strength/ISO 180/4A | Izod impact strength notched (23°C) | ISO 180/4A | KJ/m^2 | 60 | - |
Izod impact strength notched (-20℃) | ISO 180/4A | KJ/m^2 | 10 | - | |
Yield Strain Yield Strain/ISO 527-1/-2 | Yield Strain | ISO 527-1/-2 | % | 6 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Volume resistivity Volume resistivity/IEC 60093 | Volume resistivity | IEC 60093 | Ω・cm | NaN | - |
Surface resistance Surface resistance/IEC 60093 | Surface resistance | IEC 60093 | Ω | NaN | - |
Dielectric constant Dielectric constant/ASTM D2520 | Dielectric constant (DK, 1GHz) | ASTM D2520 | - | 2.8 | - |
Dielectric constant (DK, 2.5GHz) | ASTM D2520 | - | 2.8 | - | |
Dielectric constant (DK, 6GHz) | ASTM D2520 | - | 2.8 | - | |
Dielectric loss tangent Dielectric loss tangent/ASTM D2520 | Dissipation factor (DF, 1GHz) | ASTM D2520 | 0.005 | - | |
Dielectric loss tangent (DK, 2.5GHz) | ASTM D2520 | 0.005 | - | ||
Dissipation factor (DF, 6GHz) | ASTM D2520 | 0.005 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/ISO 294-4 | Mold shrinkage (machine direction) | ISO 294-4 | % | 0.5 | - |
ＭＶＲ ＭＶＲ/ISO 1133 | Melt volume flow rate (300℃, 1.20kg) | ISO 1133 | cm3/10min | 14 | - |
| Key Features |
|---|
Laser irradiated three-dimensional circuit formation (LDS), low viscosity, flame retardant (halogen-free), only available in black |