| Manufacturer | Asahi Kasei Corporation |
| Resin Name | PA66 |
| Product Name | LEONA |
| ISO Material Code | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ISO1183 | Density | ISO1183 | g/cm^3 | 1.39 | - |
Proportion | ASTMD792 | 1.39 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Deflection Temperature under Load Deflection Temperature under Load/ISO75 | Deflection temperature under load (load 1.8 MPa) | ISO75 | ℃ | 210 | - |
Deflection temperature under load (load 0.45 MPa) | ISO75 | ℃ | 230 | - | |
Deflection temperature under load (load 1.82 MPa) | ASTMD648 | ℃ | 210 | - | |
Linear expansion coefficient Linear expansion coefficient/ASTMD 696 | Linear expansion coefficient | ASTMD 696 | ×10^-5/℃ | 3 | - |
Flammability Flammability/UL94 | UL-94 (1/32 inch, 0.75 mm) | UL94 | NaN | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile breaking stress Tensile breaking stress/ISO527 | Tensile breaking stress (23℃ 50% RH) | ISO527 | MPa | 174 | - |
Tensile strain at break Tensile strain at break/ISO527 | Tensile breaking strain (23℃ 50%RH) | ISO527 | % | 5.5 | - |
Tensile Modulus Tensile Modulus/ISO527 | Tensile modulus (Young's modulus, 23℃ 50% RH) | ISO527 | MPa | 9400 | - |
Bending strength Bending strength/ISO178 | Bending strength (23℃ 50% RH) | ISO178 | MPa | 233 | - |
Bending strength | ASTMD790 | MPa | 275 | - | |
Flexural modulus Flexural modulus/ISO178 | Flexural modulus (23℃) | ISO178 | MPa | 7300 | - |
Flexural modulus | ASTMD790 | MPa | 8600 | - | |
Charpy impact strength Charpy impact strength/ISO179 | Charpy impact strength (unnotched) | ISO179 | KJ/m^2 | 98 | - |
Charpy impact strength (notched) | ISO179 | KJ/m^2 | 12 | - | |
Izod impact strength Izod impact strength/ASTMD256 | Izod impact value (23℃ 1/4 inch notched) | ASTMD256 | J/m | 132 | - |
Surface hardness Surface hardness/ISO2039 | Rockwell hardness (M scale) | ISO2039 | M | 90 | - |
Rockwell hardness (M scale) | ASTMD785 | M | 90 | - | |
Tensile strength Tensile strength/ASTMD638 | Tensile strength | ASTMD638 | MPa | 167 | - |
Tensile elongation Tensile elongation/ASTMD638 | Tensile elongation | ASTMD638 | % | 4 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/Asahi Kasei Process | Mold shrinkage (flow direction/transverse direction) | Asahi Kasei Process | % | 0.3 | - |
Molding shrinkage (flow direction/right angle direction) (3mm) | Asahi Kasei Process | % | 0.3 | - | |
Mold shrinkage rate TD Mold shrinkage rate TD/Asahi Kasei Process | Mold shrinkage (flow direction/transverse direction) | Asahi Kasei Process | % | 0.8 | - |
Molding shrinkage (flow direction/right angle direction) (3mm) | Asahi Kasei Process | % | 0.8 | - |
| Key Features |
|---|
GF reinforced, good appearance, high rigidity |