| Manufacturer | Asahi Kasei Corporation |
| Resin Name | PA66 |
| Product Name | LEONA |
| ISO Material Code | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ISO1183 | Density | ISO1183 | g/cm^3 | 1.68 | - |
Proportion | ASTMD792 | 1.68 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Deflection Temperature under Load Deflection Temperature under Load/ISO75 | Deflection temperature under load (load 1.8 MPa) | ISO75 | ℃ | 220 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile breaking stress Tensile breaking stress/ISO527 | Tensile breaking stress (23℃ 50% RH) | ISO527 | MPa | 180 | - |
Tensile strain at break Tensile strain at break/ISO527 | Tensile breaking strain (23℃ 50%RH) | ISO527 | % | 3 | - |
Tensile Modulus Tensile Modulus/ISO527 | Tensile modulus (Young's modulus, 23℃ 50% RH) | ISO527 | MPa | 15000 | - |
Bending strength Bending strength/ISO178 | Bending strength (23℃ 50% RH) | ISO178 | MPa | 250 | - |
Bending strength | ASTMD790 | MPa | 262 | - | |
Flexural modulus Flexural modulus/ISO178 | Flexural modulus (23℃) | ISO178 | MPa | 14000 | - |
Flexural modulus | ASTMD790 | MPa | 13900 | - | |
Charpy impact strength Charpy impact strength/ISO179 | Charpy impact strength (notched) | ISO179 | KJ/m^2 | 5 | - |
Izod impact strength Izod impact strength/ASTMD256 | Izod impact value (23℃ 1/4 inch notched) | ASTMD256 | J/m | 54 | - |
Surface hardness Surface hardness/ISO2039 | Rockwell hardness (R scale) | ISO2039 | R | 120 | - |
Rockwell hardness (M scale) | ISO2039 | M | 102 | - | |
Rockwell hardness (R scale) | ASTMD785 | R | 120 | - | |
Rockwell hardness (M scale) | ASTMD785 | M | 102 | - | |
Tensile strength Tensile strength/ASTMD638 | Tensile strength | ASTMD638 | MPa | 191 | - |
Tensile elongation Tensile elongation/ASTMD638 | Tensile elongation | ASTMD638 | % | 4 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/Asahi Kasei Process | Mold shrinkage (flow direction/transverse direction) | Asahi Kasei Process | % | 0.2 | - |
Molding shrinkage (flow direction/right angle direction) (3mm) | Asahi Kasei Process | % | 0.2 | - | |
Mold shrinkage rate TD Mold shrinkage rate TD/Asahi Kasei Process | Mold shrinkage (flow direction/transverse direction) | Asahi Kasei Process | % | 1 | - |
Molding shrinkage (flow direction/right angle direction) (3mm) | Asahi Kasei Process | % | 1 | - |
| Key Features |
|---|
Filler reinforcement, good appearance, high rigidity |