| Manufacturer | Asahi Kasei Corporation |
| Resin Name | PA66 |
| Product Name | LEONA |
| ISO Material Code | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ISO1183 | Density | ISO1183 | g/cm^3 | 1.08 | - |
Proportion | ASTMD792 | 1.08 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Deflection Temperature under Load Deflection Temperature under Load/ISO75 | Deflection temperature under load (load 1.8 MPa) | ISO75 | ℃ | 58 | - |
Deflection temperature under load (load 0.45 MPa) | ISO75 | ℃ | 183 | - | |
Deflection temperature under load (load 1.82 MPa) | ASTMD648 | ℃ | 73 | - | |
Deflection temperature under load (load 0.46 MPa) | ASTMD648 | ℃ | 215 | - | |
Linear expansion coefficient Linear expansion coefficient/ASTMD 696 | Linear expansion coefficient | ASTMD 696 | ×10^-5/℃ | 11 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile Yield Stress Tensile Yield Stress/ISO527 | Tensile yield stress (23℃ 50% RH) | ISO527 | MPa | 53 | - |
Tensile breaking stress Tensile breaking stress/ISO527 | Tensile breaking stress (23℃ 50% RH) | ISO527 | MPa | 45 | - |
Tensile strain at break Tensile strain at break/ISO527 | Tensile yield strain (23℃ 50% RH) | ISO527 | % | 5.5 | - |
Tensile breaking strain (23℃ 50%RH) | ISO527 | % | 60 | - | |
Tensile Modulus Tensile Modulus/ISO527 | Tensile modulus (Young's modulus, 23℃ 50% RH) | ISO527 | MPa | 1900 | - |
Bending strength Bending strength/ISO178 | Bending strength (23℃ 50% RH) | ISO178 | MPa | 73 | - |
Bending strength | ASTMD790 | MPa | 79 | - | |
Flexural modulus Flexural modulus/ISO178 | Flexural modulus (23℃) | ISO178 | MPa | 2000 | - |
Flexural modulus | ASTMD790 | MPa | 2000 | - | |
Charpy impact strength Charpy impact strength/ISO179 | Charpy impact strength (unnotched) | ISO179 | KJ/m^2 | NB | |
Charpy impact strength (notched) | ISO179 | KJ/m^2 | 80 | - | |
Izod impact strength Izod impact strength/ASTMD256 | Izod impact value (23℃ 1/4 inch notched) | ASTMD256 | J/m | 1110 | - |
Surface hardness Surface hardness/ISO2039 | Rockwell hardness (R scale) | ISO2039 | R | 107 | - |
Rockwell hardness (R scale) | ASTMD785 | R | 107 | - | |
Tensile strength Tensile strength/ASTMD638 | Tensile strength | ASTMD638 | MPa | 54 | - |
Tensile elongation Tensile elongation/ASTMD638 | Tensile elongation | ASTMD638 | % | 70 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage Mold shrinkage/Asahi Kasei Process | Mold shrinkage (flow direction/transverse direction) | Asahi Kasei Process | % | - | |
Molding shrinkage (flow direction/right angle direction) (3mm) | Asahi Kasei Process | % | - |
| Key Features |
|---|
Long term heat resistance |