| Manufacturer | Toray Industries, Inc. |
| Resin Name | PA66 |
| Product Name | Amilan |
| ISO Material Code | >PA66-MD40< |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ISO 1183 | Density (23℃) | ISO 1183 | g/cm^3 | 1.51 | - |
Water absorption Water absorption/ISO 62 | Water absorption, in water (24hr, 23℃) | ISO 62 | % | 0.6 | - |
Water absorption, in water (saturated, 23℃) | ISO 62 | % | 5.1 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Deflection Temperature under Load Deflection Temperature under Load/ISO 75-2/B | Deflection temperature under load (0.45MPa, no annealing) | ISO 75-2/B | ℃ | 243 | - |
Deflection temperature under load (1.8MPa, no annealing) | ISO 75-2/A | ℃ | 185 | - | |
Melting point Melting point/DSC method | Dissolving temperature | DSC method | ℃ | 265 | - |
Flammability Flammability/Toray method | Flammability rating, UL 94 | Toray method | NaN | Quite |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile strain at break Tensile strain at break/ISO 527-2 | Tensile strain (break point, -40℃) | ISO 527-2 | % | 3 | - |
Tensile strain (break point, 23℃) | ISO 527-2 | % | 3.5 | - | |
Tensile strain (break point, 80℃) | ISO 527-2 | % | 5 | - | |
Bending strength Bending strength/ISO 178 | Bending strength (-40℃) | ISO 178 | MPa | 185 | - |
Bending strength (23℃) | ISO 178 | MPa | 155 | - | |
Bending strength (80℃) | ISO 178 | MPa | 65 | - | |
Flexural modulus Flexural modulus/ISO 178 | Flexural modulus (-40℃) | ISO 178 | MPa | 6200 | - |
Flexural modulus (23℃) | ISO 178 | MPa | 5800 | - | |
Flexural modulus (80℃) | ISO 178 | MPa | 2000 | - | |
Charpy impact strength Charpy impact strength/ISO 179 | Charpy impact strength (notched, 23℃) | ISO 179 | kJ/m^2 | 5.5 | - |
Surface hardness Surface hardness/ISO 2039-2 | Rockwell hardness (R scale, 23℃) | ISO 2039-2 | 120 | - | |
Rockwell hardness (M scale, 23℃) | ISO 2039-2 | 83 | - | ||
Tensile strength Tensile strength/ISO 527-2 | Tensile strength (-40℃) | ISO 527-2 | MPa | 120 | - |
Tensile strength (23℃) | ISO 527-2 | MPa | 95 | - | |
Tensile strength (80℃) | ISO 527-2 | MPa | 40 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/Toray method | Mold shrinkage, parallel: 3.00mm (80×80×3mm) | Toray method | % | - | |
Mold shrinkage rate TD Mold shrinkage rate TD/Toray method | Molding shrinkage, vertical: 3.00mm (80×80×3mm) | Toray method | % | - |
| Main Applications |
|---|
Office Automation Equipment, Sporting Goods, Equipment Parts, Construction Applications, Tools/Other Parts, Auto Exterior Parts, Auto Interior Parts, Automotive Applications, Large & Small Appliances, Electrical/Electronic Equipment |
| Key Features |
|---|
Reinforced, low warpage, inorganic filler reinforcement |