| Manufacturer | Toray Industries, Inc. |
| Resin Name | PBT |
| Product Name | TORAYCON |
| ISO Material Code | >PBT+ABS< |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ISO1183 | Density (23℃) | ISO1183 | kg/m^3(×10^-3) | 1.135 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Flammability Flammability/UL94 | Flammability | UL94 | NaN | Quite |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile Modulus Tensile Modulus/ISO527-1,2 | Tensile modulus (23℃) | ISO527-1,2 | MPa | 2200 | - |
Bending strength Bending strength/ISO178 | Flexural strength (23℃) | ISO178 | MPa | 66 | - |
Flexural modulus Flexural modulus/ISO178 | Flexural modulus (MPa, 23℃) | ISO178 | MPa | 2100 | - |
Charpy impact strength Charpy impact strength/ISO179 | Charpy impact strength (notched, 23℃) | ISO179 | kJ/m^2 | 43 | - |
Tensile strength Tensile strength/ISO527-1,2 | Tensile strength (23℃) | ISO527-1,2 | MPa | 46 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/Toray method | Mold shrinkage rate (machine direction, 80 x 80 x 3 mmt) | Toray method | % | 1.1 | - |
Mold shrinkage rate TD Mold shrinkage rate TD/Toray method | Molding shrinkage rate (transverse direction, 80 x 80 x 3 mmt) | Toray method | % | 1.2 | - |
| Key Features |
|---|
Unreinforced, high impact, low warpage |