| Manufacturer | Asahi Kasei Corporation |
| Resin Name | POM |
| Product Name | Tenac |
| ISO Material Code | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ISO 1183 | Density | ISO 1183 | g/cm3 | 1.46 | - |
Water absorption Water absorption/ASTMD570 | Water absorption (23℃50％24hr in water) | ASTMD570 | % | 0.2 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Deflection Temperature under Load Deflection Temperature under Load/ISO75 | Deflection temperature under load (load 1.82 MPa) | ISO75 | ℃ | 163 | - |
Deflection temperature under load (load 0.46 MPa) | ISO75 | ℃ | 166 | - | |
Deflection temperature under load (load 1.82 MPa) | ASTMD648 | ℃ | 150 | - | |
Deflection temperature under load (load 0.46 MPa) | ASTMD648 | ℃ | 163 | - | |
Linear expansion coefficient Linear expansion coefficient/ISO 11359 | Linear expansion coefficient | ISO 11359 | ×10^-5/℃ | - | |
Linear expansion coefficient | ASTMD696 | ×10^-5/℃ | 6 | - | |
Flammability Flammability/UL94 | Flammability | UL94 | NaN | - | |
Burn rate Burn rate/UL94 | UL-94 (1/32 inch, 0.8 mm) | UL94 | NaN | 0.75mmt |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile breaking stress Tensile breaking stress/ISO527 | Tensile breaking stress | ISO527 | MPa | 130 | - |
Tensile strain at break Tensile strain at break/ISO527 | Tensile strain at break | ISO527 | % | 1 | - |
Tensile Modulus Tensile Modulus/ISO527 | Tensile Modulus | ISO527 | MPa | 13000 | - |
Bending strength Bending strength/ASTMD790 | Bending strength | ASTMD790 | MPa | 108 | - |
Flexural modulus Flexural modulus/ISO 178 | Flexural modulus | ISO 178 | MPa | 12500 | - |
Flexural modulus | ASTMD790 | MPa | 12200 | - | |
Charpy impact strength Charpy impact strength/ISO179 | Charpy impact strength (notched) | ISO179 | KJ/m^2 | 5 | - |
Izod impact strength Izod impact strength/ASTMD256 | Izod impact value (notched) | ASTMD256 | J/m | 39 | - |
Surface hardness Surface hardness/ASTMD785 | Rockwell hardness (M scale) | ASTMD785 | M | 98 | - |
Tensile strength Tensile strength/ASTMD638 | Tensile strength | ASTMD638 | MPa | 60 | - |
Tensile elongation Tensile elongation/ASTMD638 | Tensile elongation | ASTMD638 | % | 7 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/Asahi Kasei Process | Mold shrinkage (flow direction/transverse direction) | Asahi Kasei Process | % | - | |
Mold shrinkage rate TD Mold shrinkage rate TD/Asahi Kasei Process | Mold shrinkage (flow direction/transverse direction) | Asahi Kasei Process | % | - | |
ＭＦＲ ＭＦＲ/ISO1133 | Melt Mass Flow Rate | ISO1133 | g/10min | 4 | - |
| Key Features |
|---|
Copolymer, Carbon Fiber Reinforced |