| Manufacturer | Polypla Evonik Co., Ltd. |
| Resin Name | PA12 |
| Product Name | DAIAMID |
| ISO Material Code | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ISO1183 | Density | ISO1183 | g/cm^3 | 1.02 | 23℃ |
Water absorption Water absorption/ISO62 | Water absorption | ISO62 | % | 0.6 | 50%,Balance |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Deflection Temperature under Load Deflection Temperature under Load/ISO75 | Heat distortion temperature (1.8MPa) | ISO75 | ℃ | 50 | DRY |
Heat distortion temperature (0.45MPa) | ISO75 | ℃ | 120 | DRY | |
Melting point Melting point/ISO11357 | Melting point | ISO11357 | ℃ | 178 | DSC2ndheating |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile breaking stress Tensile breaking stress/ISO527 | Tensile Break Strength | ISO527 | MPa | 60 | 23℃,50%RH |
Tensile strain at break Tensile strain at break/ISO527 | Tensile elongation at break | ISO527 | % | 50 | 23℃,50%RH |
Tensile Modulus Tensile Modulus/ISO527 | Tensile Modulus | ISO527 | MPa | 1300 | 23℃,50%RH |
Charpy impact strength Charpy impact strength/ISO179 | Charpy impact strength (notched at 23°C) | ISO179 | kJ/m^2 | NB | |
Charpy impact strength (notched -30℃) | ISO179 | kJ/m^2 | NB |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
MVR MVR/ISO1133 | MVR | ISO1133 | cm^3/10min | 10 | 190℃ |
MVR | ISO1133 | cm^3/10min | 10 | 230℃ |