| Manufacturer | Solvay Specialty Polymers Japan Co., Ltd. |
| Resin Name | PPA |
| Product Name | Amodel |
| ISO Material Code | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ISO1183/A | Density | ISO1183/A | g/cm＾3 | 1.59 | - |
Water absorption Water absorption/ASTMD570 | Water absorption rate (24hr) | ASTMD570 | % | 0.19 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Deflection Temperature under Load Deflection Temperature under Load/ASTMD648 | Deflection temperature under load (0.45MPa, no annealing treatment) | ASTMD648 | ℃ | 290 | - |
Linear expansion coefficient (flow) Linear expansion coefficient (flow)/ASTME831 | Linear expansion coefficient (flow, 0 to 100℃) | ASTME831 | ×10＾-5/℃ | 25 | - |
Linear expansion coefficient (flow, 150 to 250℃) | ASTME831 | ×10＾-5/℃ | 19 | - | |
Linear expansion coefficient (right angle) Linear expansion coefficient (right angle)/ASTME228 | Linear expansion coefficient (right angle, 0 to 100℃) | ASTME228 | ×10＾-5/℃ | 96 | - |
Linear expansion coefficient (right angle, 150 to 250℃) | ASTME228 | ×10＾-5/℃ | 150 | - | |
Melting point Melting point/ASTMD3418 | Melting point | ASTMD3418 | ℃ | 323 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile strain at break Tensile strain at break/ASTMD638 | Tensile elongation at break | ASTMD638 | % | 1.2 | - |
Tensile Modulus Tensile Modulus/ASTMD638 | Tensile Modulus | ASTMD638 | MPa | 9100 | - |
Bending strength Bending strength/ASTMD790 | Bending strength | ASTMD790 | MPa | 165 | - |
Flexural modulus Flexural modulus/ASTMD790 | Flexural modulus | ASTMD790 | MPa | 8100 | - |
Izod impact strength Izod impact strength/ASTMD256 | Izod impact strength (notched) | ASTMD256 | J/m | 18 | - |
Surface hardness Surface hardness/ASTMD785 | Rockwell Hardness | ASTMD785 | R | 124 | - |
Tensile strength Tensile strength/ASTMD638 | Tensile stress | ASTMD638 | MPa | 104 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/ASTMD955 | Mold shrinkage rate MD | ASTMD955 | % | 0.4 | - |
Mold shrinkage rate TD Mold shrinkage rate TD/ASTMD955 | Mold shrinkage rate TD | ASTMD955 | % | 0.6 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Resin temperature Resin temperature/ | Resin temperature | ℃ | - | ||
Mold Temperature Mold Temperature/ | Mold Temperature | ℃ | - | ||
Drying conditions Drying conditions/ | Drying conditions | ℃ | 120 | 4.0hr |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Filler Content Filler Content/ | Filler content (GF) | % | 22 | - |
| Color |
|---|
White |
| Main Applications |
|---|
Automobiles, Automotive Electronics Parts |
| Key Features |
|---|
Chemical resistance, high speed molding cycle, color stability, high reflectance, high rigidity, light stability, low moisture absorption |