| Manufacturer | Solvay Specialty Polymers Japan Co., Ltd. |
| Resin Name | PPA |
| Product Name | Amodel |
| ISO Material Code | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ISO1183/A | Density | ISO1183/A | g/cm＾3 | 1.75 | - |
Water absorption Water absorption/ISO62 | Water absorption rate (23℃, 24hr) | ISO62 | % | 0.19 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Deflection Temperature under Load Deflection Temperature under Load/ISO75-2/Af | Deflection temperature under load (1.8MPa, no annealing treatment) | ISO75-2/Af | ℃ | 304 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile breaking stress Tensile breaking stress/ISO527-2 | Tensile strength at break (23℃) | ISO527-2 | MPa | 244 | - |
Tensile strength at break (200℃) | ISO527-2 | MPa | 79.6 | - | |
Tensile strain at break Tensile strain at break/ISO527-2 | Tensile elongation at break (23℃) | ISO527-2 | % | 1.4 | - |
Tensile elongation at break (200℃) | ISO527-2 | % | 3.3 | - | |
Tensile Modulus Tensile Modulus/ISO527-2 | Tensile modulus (23℃) | ISO527-2 | MPa | 23300 | - |
Tensile modulus (200℃) | ISO527-2 | MPa | 8770 | - | |
Bending strength Bending strength/ISO178 | Bending stress (23℃) | ISO178 | MPa | 385 | - |
Bending stress (200℃) | ISO178 | MPa | 137 | - | |
Flexural modulus Flexural modulus/ISO178 | Flexural modulus (23℃) | ISO178 | MPa | 19300 | - |
Flexural modulus (200℃) | ISO178 | MPa | 8500 | - | |
Charpy impact strength Charpy impact strength/ISO179/1eU | Charpy impact strength (unnotched, 23℃) | ISO179/1eU | kJ/m＾2 | 130 | - |
Charpy impact strength (notched, 23℃) | ISO179/1eA | kJ/m＾2 | 13 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/ISO294-4 | Mold shrinkage rate MD | ISO294-4 | % | 0.5 | - |
Mold shrinkage rate TD Mold shrinkage rate TD/ISO294-4 | Mold shrinkage rate TD | ISO294-4 | % | 0.8 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Resin temperature Resin temperature/ | Resin temperature | ℃ | - | ||
Mold Temperature Mold Temperature/ | Mold Temperature | ℃ | - | ||
Drying conditions Drying conditions/ | Drying conditions | ℃ | 120 | 4.0hr |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Filler Content Filler Content/ | Filler content (GF) | % | 60 | - |
| Color |
|---|
Black |
| Main Applications |
|---|
Automotive, Automotive Electronics, Automotive Parts, Cameras, Mobile Phones, Connectors, Electrical/Electronic, Housings, Industrial Applications, Machinery/Machinery Parts, Metal Substitutes, Transmission Applications |
| Key Features |
|---|
Chemical resistance, creep resistance, fast molding cycle, good dimensional stability, high strength, thermal stability, high heat resistance, high strength, hot water moldability, low CLTE, lubrication, ultra-high toughness |