Public Beta
Public Beta
| Manufacturer | Solvay Specialty Polymers Japan Co., Ltd. |
| Resin Name | PPA |
| Product Name | Amodel |
| ISO Material Code | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ISO1183/A | Density | ISO1183/A | g/cm＾3 | 1.6 | - |
Water absorption Water absorption/ASTMD570 | Water absorption rate (24hr) | ASTMD570 | % | 0.2 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Deflection Temperature under Load Deflection Temperature under Load/ISO75-2/B | Deflection temperature under load (0.45MPa, no annealing treatment) | ISO75-2/B | ℃ | 306 | - |
Linear expansion coefficient (flow) Linear expansion coefficient (flow)/ASTME831 | Linear expansion coefficient (flow, 50 to 100℃) | ASTME831 | ×10＾-5/℃ | 3.1 | - |
Linear expansion coefficient (flow, 100 to 150℃) | ASTME831 | ×10＾-5/℃ | 3.8 | - | |
Linear expansion coefficient (flow, 150 to 200℃) | ASTME831 | ×10＾-5/℃ | 2.7 | - | |
Linear expansion coefficient (flow, 200 to 250℃) | ASTME831 | ×10＾-5/℃ | 3.1 | - | |
Linear expansion coefficient (right angle) Linear expansion coefficient (right angle)/ASTME831 | Linear expansion coefficient (right angle, 50 to 100℃) | ASTME831 | ×10＾-5/℃ | 6.3 | - |
Linear expansion coefficient (right angle, 100 to 150℃) | ASTME831 | ×10＾-5/℃ | 10 | - | |
Linear expansion coefficient (right angle, 150 to 200℃) | ASTME831 | ×10＾-5/℃ | 13 | - | |
Linear expansion coefficient (right angle, 200 to 250℃) | ASTME831 | ×10＾-5/℃ | 15 | - | |
Melting point Melting point/ISO11357-3 | Melting point | ISO11357-3 | ℃ | 324 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile strain at break Tensile strain at break/ISO527-2 | Tensile elongation at break | ISO527-2 | % | 1.3 | - |
Tensile Modulus Tensile Modulus/ISO527-2 | Tensile Modulus | ISO527-2 | MPa | 9100 | - |
Bending strength Bending strength/ISO178 | Bending stress | ISO178 | MPa | 171 | - |
Flexural modulus Flexural modulus/ISO178 | Flexural modulus | ISO178 | MPa | 7790 | - |
Izod impact strength Izod impact strength/ISO180/1A | Izod impact strength (notched) | ISO180/1A | kJ/m＾2 | 2.9 | - |
Tensile strength Tensile strength/ASTMD638 | Tensile strength | ASTMD638 | MPa | 102 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/ASTMD955 | Mold shrinkage rate MD | ASTMD955 | % | 0.5 | - |
Mold shrinkage rate TD Mold shrinkage rate TD/ASTMD955 | Mold shrinkage rate TD | ASTMD955 | % | 0.6 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Resin temperature Resin temperature/ | Resin temperature | ℃ | - | ||
Mold Temperature Mold Temperature/ | Mold Temperature | ℃ | - | ||
Drying conditions Drying conditions/ | Drying conditions | ℃ | 120 | 4.0hr |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Filler Content Filler Content/ | Filler content (MR) | % | 22 | - |
| Color |
|---|
White |
| Main Applications |
|---|
Automotive, Automotive Electronics, LED |
| Key Features |
|---|
Chemical resistance, high speed molding cycle, color stability, high reflectance, high rigidity, light stability, low moisture absorption |
Copyright© 2026 PlaBase. All Rights Reserved.