| Manufacturer | Solvay Specialty Polymers Japan Co., Ltd. |
| Resin Name | PPA |
| Product Name | Amodel |
| ISO Material Code | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ISO1183/A | Density | ISO1183/A | g/cm＾3 | 1.45 | - |
Water absorption Water absorption/ISO62 | Water absorption rate (23℃, 24hr) | ISO62 | % | 0.29 | - |
Water absorption rate (24hr) | ASTMD570 | % | 0.3 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Deflection Temperature under Load Deflection Temperature under Load/ISO75-2/B | Deflection temperature under load (0.45MPa, no annealing treatment) | ISO75-2/B | ℃ | 303 | - |
Deflection temperature under load (1.8MPa, no annealing treatment) | ISO75-2/A | ℃ | 288 | - | |
Deflection temperature under load (1.8MPa, annealed, 3.20mm) | ASTMD648 | ℃ | 291 | - | |
Linear expansion coefficient (flow) Linear expansion coefficient (flow)/ASTME831 | Linear expansion coefficient (flow, 0 to 100℃) | ASTME831 | ×10＾-5/℃ | 2.2 | - |
Linear expansion coefficient (flow, 100 to 200℃) | ASTME831 | ×10＾-5/℃ | 1.6 | - | |
Linear expansion coefficient (right angle) Linear expansion coefficient (right angle)/ASTME831 | Linear expansion coefficient (right angle, 0 to 100℃) | ASTME831 | ×10＾-5/℃ | 6.1 | - |
Linear expansion coefficient (right angle, 100 to 200℃) | ASTME831 | ×10＾-5/℃ | 10 | - | |
Melting point Melting point/ISO11357-3 | Melting point | ISO11357-3 | ℃ | 310 | - |
Melting point | ASTMD570 | ℃ | 310 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile breaking stress Tensile breaking stress/ISO527-2 | Tensile breaking stress (23℃) | ISO527-2 | MPa | 211 | - |
Tensile breaking stress (100℃) | ISO527-2 | MPa | 121 | - | |
Tensile breaking stress (150℃) | ISO527-2 | MPa | 92.4 | - | |
Tensile breaking stress (175℃) | ISO527-2 | MPa | 82 | - | |
Tensile strain at break Tensile strain at break/ISO527-2 | Tensile elongation at break (23℃) | ISO527-2 | % | 2 | - |
Tensile elongation at break (100℃) | ISO527-2 | % | 4.3 | - | |
Tensile elongation at break (150℃) | ISO527-2 | % | 4.9 | - | |
Tensile elongation at break (175℃) | ISO527-2 | % | 4.7 | - | |
Tensile elongation at break | ASTMD638 | % | 1.9 | - | |
Tensile Modulus Tensile Modulus/ISO527-2 | Tensile modulus (23℃) | ISO527-2 | MPa | 11500 | - |
Tensile modulus (100℃) | ISO527-2 | MPa | 7310 | - | |
Tensile modulus (150℃) | ISO527-2 | MPa | 6270 | - | |
Tensile modulus (175℃) | ISO527-2 | MPa | 5310 | - | |
Tensile Modulus | ASTMD638 | MPa | 13800 | - | |
Bending strength Bending strength/ASTMD790 | Bending strength | ASTMD790 | MPa | 310 | - |
Bending strength (3.5% strain, 23℃) | ISO178 | MPa | 300 | - | |
Bending strength (3.5% strain, 100℃) | ISO178 | MPa | 170 | - | |
Bending strength (3.5% strain, 150℃) | ISO178 | MPa | 123 | - | |
Bending strength (3.5% strain, 175℃) | ISO178 | MPa | 112 | - | |
Flexural modulus Flexural modulus/ISO178 | Flexural modulus (23℃) | ISO178 | MPa | 11400 | - |
Flexural modulus (100℃) | ISO178 | MPa | 6600 | - | |
Flexural modulus (150℃) | ISO178 | MPa | 4900 | - | |
Flexural modulus (175℃) | ISO178 | MPa | 4600 | - | |
Flexural modulus | ASTMD790 | MPa | 11400 | - | |
Charpy impact strength Charpy impact strength/ISO179/1eU | Charpy impact strength (unnotched, 23℃) | ISO179/1eU | kJ/m＾2 | 60 | - |
Charpy impact strength (notched, 23℃) | ISO179/1eA | kJ/m＾2 | 9.2 | - | |
Izod impact strength Izod impact strength/ISO180 | Izod impact strength (unnotched, 23℃) | ISO180 | kJ/m＾2 | 62 | - |
Izod impact strength (notched, 23℃) | ISO180 | kJ/m＾2 | 9.1 | - | |
Izod impact strength (unnotched) | ASTMD256 | J/m | 800 | - | |
Izod impact strength (notched) | ASTMD256 | J/m | 85 | - | |
Surface hardness Surface hardness/ASTMD785 | Rockwell Hardness | ASTMD785 | R | 125 | - |
Tensile strength Tensile strength/ASTMD638 | Tensile stress | ASTMD638 | MPa | 203 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/ISO294-4 | Mold shrinkage rate MD | ISO294-4 | % | 0.5 | - |
Mold shrinkage rate MD | ASTMD955 | % | 0.6 | - | |
Mold shrinkage rate TD Mold shrinkage rate TD/ISO294-4 | Mold shrinkage rate TD | ISO294-4 | % | 1 | - |
Mold shrinkage rate TD | ASTMD955 | % | 0.9 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Resin temperature Resin temperature/ | Resin temperature | ℃ | - | ||
Mold Temperature Mold Temperature/ | Mold Temperature | ℃ | - | ||
Drying conditions Drying conditions/ | Drying conditions | ℃ | 120 | 4.0hr |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Filler Content Filler Content/ | Filler content (GF) | % | 35 | - |
| Color |
|---|
Black |
| Main Applications |
|---|
Automotive,Auto Electronics,Auto Parts,Connectors,Electrified Housing,Electrical/Electronic,General Purpose,Housing,Industrial Application,Industrial Parts,Lawn Mowers,Machinery/Machine Parts,Metal Replacement,Power Supply/Other Tools,Valves/Valve Parts |
| Key Features |
|---|
Chemical resistance, creep resistance, high flow, high rigidity, thermal stability, high heat resistance, high rigidity, high strength, hot water moldability, low moisture absorption |