| Manufacturer | Solvay Specialty Polymers Japan Co., Ltd. |
| Resin Name | PPA |
| Product Name | Amodel |
| ISO Material Code | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ISO1183/A | Density | ISO1183/A | g/cm＾3 | 1.84 | - |
Water absorption Water absorption/ASTMD570 | Water absorption rate (24hr) | ASTMD570 | % | 0.1 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Deflection Temperature under Load Deflection Temperature under Load/ISO75-2/A | Deflection temperature under load (1.8MPa, no annealing treatment) | ISO75-2/A | ℃ | 280 | - |
Deflection temperature under load (1.8MPa, annealed) | ASTMD648 | ℃ | 278 | - | |
Linear expansion coefficient (flow) Linear expansion coefficient (flow)/ASTME831 | Linear expansion coefficient (flow, 0 to 100℃) | ASTME831 | ×10＾-5/℃ | 1.7 | - |
Linear expansion coefficient (flow, 100 to 200℃) | ASTME831 | ×10＾-5/℃ | 1.7 | - | |
Linear expansion coefficient (right angle) Linear expansion coefficient (right angle)/ASTME831 | Linear expansion coefficient (right angle, 0 to 100℃) | ASTME831 | ×10＾-5/℃ | 4 | - |
Linear expansion coefficient (right angle, 100 to 200℃) | ASTME831 | ×10＾-5/℃ | 7.2 | - | |
Melting point Melting point/ISO11357-3 | Melting point | ISO11357-3 | ℃ | 311 | - |
Melting point | ASTMD3418 | ℃ | 311 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile breaking stress Tensile breaking stress/ISO527-2 | Tensile breaking stress (23℃) | ISO527-2 | MPa | 200 | - |
Tensile breaking stress (100℃) | ISO527-2 | MPa | 127 | - | |
Tensile breaking stress (150℃) | ISO527-2 | MPa | 52.4 | - | |
Tensile breaking stress (175℃) | ISO527-2 | MPa | 43.4 | - | |
Tensile breaking stress | ASTMD638 | MPa | 207 | - | |
Tensile strain at break Tensile strain at break/ISO527-2 | Tensile elongation at break (23℃) | ISO527-2 | % | 1.4 | - |
Tensile elongation at break (100℃) | ISO527-2 | % | 1.5 | - | |
Tensile elongation at break (150℃) | ISO527-2 | % | 3.4 | - | |
Tensile elongation at break (175℃) | ISO527-2 | % | 3.1 | - | |
Tensile elongation at break | ASTMD638 | % | 1.7 | - | |
Tensile Modulus Tensile Modulus/ISO527-2 | Tensile modulus (23℃) | ISO527-2 | MPa | 22500 | - |
Tensile modulus (100℃) | ISO527-2 | MPa | 17200 | - | |
Tensile modulus (150℃) | ISO527-2 | MPa | 7310 | - | |
Tensile modulus (175℃) | ISO527-2 | MPa | 6210 | - | |
Tensile Modulus | ASTMD638 | MPa | 20000 | - | |
Bending strength Bending strength/ISO178 | Bending strength (23℃) | ISO178 | MPa | 284 | - |
Bending strength (100℃) | ISO178 | MPa | 205 | - | |
Bending strength (150℃) | ISO178 | MPa | 95.8 | - | |
Bending strength (175℃) | ISO178 | MPa | 75.8 | - | |
Bending strength (yield) Bending strength (yield)/ASTMD790 | Bending strength (yield) | ASTMD790 | MPa | 290 | - |
Flexural modulus Flexural modulus/ISO178 | Flexural modulus (23℃) | ISO178 | MPa | 20500 | - |
Flexural modulus (100℃) | ISO178 | MPa | 16800 | - | |
Flexural modulus (150℃) | ISO178 | MPa | 7310 | - | |
Flexural modulus (175℃) | ISO178 | MPa | 6410 | - | |
Flexural modulus | ASTMD790 | MPa | 18600 | - | |
Charpy impact strength Charpy impact strength/ISO179/1eU | Charpy impact strength (unnotched, 23℃) | ISO179/1eU | kJ/m＾2 | 34 | - |
Charpy impact strength (notched, 23℃) | ISO179/1eA | kJ/m＾2 | 6.1 | - | |
Izod impact strength Izod impact strength/ISO180/1U | Izod impact strength (unnotched, 23℃) | ISO180/1U | kJ/m＾2 | 44 | - |
Izod impact strength (notched, 23℃) | ISO180/1A | kJ/m＾2 | 6.5 | - | |
Izod impact strength (unnotched) | ASTMD256 | J/m | 590 | - | |
Izod impact strength (notched) | ASTMD256 | J/m | 64 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/ASTMD955 | Mold shrinkage rate MD | ASTMD955 | % | 0.3 | - |
Mold shrinkage rate TD Mold shrinkage rate TD/ASTMD955 | Mold shrinkage rate TD | ASTMD955 | % | 0.5 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Resin temperature Resin temperature/ | Resin temperature | ℃ | - | ||
Mold Temperature Mold Temperature/ | Mold Temperature | ℃ | 135 | - | |
Drying conditions Drying conditions/ | Drying conditions | ℃ | 120 | 4.0hr |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Filler Content Filler Content/ | Filler content (Glass/Mineral) | % | 65 | - |
| Color |
|---|
Black, Natural |
| Main Applications |
|---|
Automotive,Auto Electronics,Automotive Parts,General Purpose,Housings,Industrial Applications,Industrial Parts,Lawn Mowers,Machinery & Machinery Parts,Metal Replacement,Power Supplies/Other Tools,Thick Wall Parts,Valves/Valve Parts |
| Key Features |
|---|
Chemical resistance, creep resistance, good dimensional stability, high strength, thermal stability, high heat resistance, high strength, low CLTE, ultra-high toughness |