| Manufacturer | Solvay Specialty Polymers Japan Co., Ltd. |
| Resin Name | PPA |
| Product Name | Amodel |
| ISO Material Code | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ISO1183/A | Density | ISO1183/A | g/cm＾3 | 1.35 | - |
Water absorption Water absorption/ASTMD570 | Water absorption rate (24hr) | ASTMD570 | % | 0.2 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Deflection Temperature under Load Deflection Temperature under Load/ISO75-2/A | Deflection temperature under load (1.8MPa, no annealing treatment) | ISO75-2/A | ℃ | 280 | - |
Deflection temperature under load (0.45MPa, no annealing treatment) | ASTMD648 | ℃ | 279 | - | |
Deflection temperature under load (1.8MPa, no annealing treatment) | ASTMD648 | ℃ | 235 | - | |
Melting point Melting point/ISO11357-3 | Melting point | ISO11357-3 | ℃ | 311 | - |
Melting point | ASTMD3418 | ℃ | 311 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile breaking stress Tensile breaking stress/ISO527-2 | Tensile breaking stress | ISO527-2 | MPa | 190 | - |
Tensile breaking stress | ASTMD638 | MPa | 174 | - | |
Tensile strain at break Tensile strain at break/ISO527-2 | Tensile elongation at break | ISO527-2 | % | 2.5 | - |
Tensile elongation at break | ASTMD638 | % | 3.2 | - | |
Tensile Modulus Tensile Modulus/ISO527-2 | Tensile Modulus | ISO527-2 | MPa | 8890 | - |
Tensile Modulus | ASTMD638 | MPa | 8480 | - | |
Bending strength Bending strength/ISO178 | Bending strength | ISO178 | MPa | 240 | - |
Bending strength (yield) Bending strength (yield)/ASTMD790 | Bending strength (yield) | ASTMD790 | MPa | 255 | - |
Flexural modulus Flexural modulus/ISO178 | Flexural modulus | ISO178 | MPa | 7790 | - |
Flexural modulus | ASTMD790 | MPa | 7580 | - | |
Charpy impact strength Charpy impact strength/ISO179/1eA | Charpy impact strength (notched) | ISO179/1eA | kJ/m＾2 | 8.8 | - |
Izod impact strength Izod impact strength/ISO180/1A | Izod impact strength (notched) | ISO180/1A | kJ/m＾2 | 8.8 | - |
Izod impact strength (unnotched) | ASTMD256 | J/m | 1100 | - | |
Izod impact strength (notched) | ASTMD256 | J/m | 120 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/ASTMD955 | Mold shrinkage rate MD | ASTMD955 | % | 0.4 | - |
Mold shrinkage rate TD Mold shrinkage rate TD/ASTMD955 | Mold shrinkage rate TD | ASTMD955 | % | 0.6 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Resin temperature Resin temperature/ | Resin temperature | ℃ | - | ||
Mold Temperature Mold Temperature/ | Mold Temperature | ℃ | 135 | - | |
Drying conditions Drying conditions/ | Drying conditions | ℃ | 121 | 4.0hr |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Filler Content Filler Content/ | Filler content (GF) | % | 25 | - |
| Color |
|---|
Black |
| Main Applications |
|---|
Home appliance parts, home appliances, automobiles, automotive electronic parts, automobile parts, bearings, connectors, piping, general purpose, housing, industrial use, industrial parts, lawn mowers, machinery and machine parts, metal replacement |
| Key Features |
|---|
Chemical resistance, good dimensional stability, thermal stability, high heat resistance, impact resistance modification |