| Manufacturer | Solvay Specialty Polymers Japan Co., Ltd. |
| Resin Name | PPA |
| Product Name | Amodel |
| ISO Material Code | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ISO1183/A | Density | ISO1183/A | g/cm＾3 | 1.13 | - |
Water absorption Water absorption/ASTMD570 | Water absorption rate (24hr) | ASTMD570 | % | 0.7 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Deflection Temperature under Load Deflection Temperature under Load/ISO75-2/A | Deflection temperature under load (1.8MPa, no annealing treatment) | ISO75-2/A | ℃ | 109 | - |
Deflection temperature under load (1.8MPa, annealed) | ASTMD648 | ℃ | 120 | - | |
Linear expansion coefficient (flow) Linear expansion coefficient (flow)/ASTME831 | Linear expansion coefficient (flow, 0 to 100℃) | ASTME831 | ×10＾-5/℃ | 7.7 | - |
Linear expansion coefficient (flow, 100 to 200℃) | ASTME831 | ×10＾-5/℃ | 14 | - | |
Linear expansion coefficient (right angle) Linear expansion coefficient (right angle)/ASTME831 | Linear expansion coefficient (right angle, 0 to 100℃) | ASTME831 | ×10＾-5/℃ | 8.1 | - |
Linear expansion coefficient (right angle, 100 to 200℃) | ASTME831 | ×10＾-5/℃ | 11 | - | |
Melting point Melting point/ISO11357-3 | Melting point | ISO11357-3 | ℃ | 310 | - |
Melting point | ASTMD3418 | ℃ | 310 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile Yield Stress Tensile Yield Stress/ISO527-2 | Tensile yield stress (23℃) | ISO527-2 | MPa | 70.3 | - |
Tensile yield stress (100℃) | ISO527-2 | MPa | 33.8 | - | |
Tensile breaking stress Tensile breaking stress/ISO527-2 | Tensile breaking stress (23℃) | ISO527-2 | MPa | 60 | - |
Tensile strain at break Tensile strain at break/ISO527-2 | Tensile elongation at break (23℃) | ISO527-2 | % | 7 | - |
Tensile elongation at break (100℃) | ISO527-2 | % | 95 | - | |
Tensile elongation at break (-40℃) | ASTMD638 | % | 12 | - | |
Tensile elongation at break (23℃) | ASTMD638 | % | 20 | - | |
Tensile Modulus Tensile Modulus/ISO527-2 | Tensile modulus (23℃) | ISO527-2 | MPa | 2410 | - |
Tensile modulus (100℃) | ISO527-2 | MPa | 2000 | - | |
Tensile Modulus | ASTMD638 | MPa | 2410 | - | |
Bending strength Bending strength/ISO178 | Bending strength (23℃) | ISO178 | MPa | 70.3 | - |
Bending strength (100℃) | ISO178 | MPa | 44.1 | - | |
Bending strength | ASTMD790 | MPa | 109 | - | |
Flexural modulus Flexural modulus/ISO178 | Flexural modulus (23℃) | ISO178 | MPa | 1790 | - |
Flexural modulus (100℃) | ISO178 | MPa | 1310 | - | |
Flexural modulus | ASTMD790 | MPa | 2280 | - | |
Charpy impact strength Charpy impact strength/ISO179/1eU | Charpy impact strength (unnotched, 23℃) | ISO179/1eU | kJ/m＾2 | No Break | |
Charpy impact strength (notched, 23℃) | ISO179/1eA | kJ/m＾2 | 78 | - | |
Izod impact strength Izod impact strength/ISO180/1U | Izod impact strength (unnotched, 23℃) | ISO180/1U | kJ/m＾2 | No Break | |
Izod impact strength (notched, 23℃) | ISO180/1A | kJ/m＾2 | 73 | - | |
Izod impact strength (notched, -40℃) | ASTMD256 | J/m | 110 | - | |
Izod impact strength (notched, 23℃) | ASTMD256 | J/m | 910 | - | |
Surface hardness Surface hardness/ASTMD785 | Rockwell Hardness | ASTMD785 | R | 120 | - |
Tensile strength Tensile strength/ASTMD638 | Tensile stress (-40℃) | ASTMD638 | MPa | 110 | - |
Tensile stress (23℃) | ASTMD638 | MPa | 68.9 | - | |
Yield Strain Yield Strain/ISO527-2 | Tensile yield elongation (23℃) | ISO527-2 | % | 5 | - |
Tensile yield elongation (100℃) | ISO527-2 | % | 4.3 | - | |
Tensile yield elongation (-40℃) | ASTMD638 | % | 9 | - | |
Tensile yield elongation (23℃) | ASTMD638 | % | 6 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/ASTMD955 | Mold shrinkage rate MD | ASTMD955 | % | 1.5 | - |
Mold shrinkage rate TD Mold shrinkage rate TD/ASTMD955 | Mold shrinkage rate TD | ASTMD955 | % | 1.5 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Resin temperature Resin temperature/ | Resin temperature | ℃ | - | ||
Mold Temperature Mold Temperature/ | Mold Temperature | ℃ | 135 | - | |
Drying conditions Drying conditions/ | Drying conditions | ℃ | 110 | 4.0hr |
| Color |
|---|
Natural |
| Main Applications |
|---|
Automotive, Auto Electronics, Auto Parts, Connectors, General Purpose, Housings, Industrial Applications, Industrial Parts, Lawn Mowers, Machinery and Machine Parts, Metal Replacement |
| Key Features |
|---|
Chemical resistance, ductility, heat stability, hot water moldability, impact resistance improvement, low warpage |