| Manufacturer | Solvay Specialty Polymers Japan Co., Ltd. |
| Resin Name | PAEK |
| Product Name | AvaSpire |
| ISO Material Code | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ASTMD792 | Proportion | ASTMD792 | 1.47 | - | |
Water absorption Water absorption/ASTMD570 | Water absorption rate (24hr) | ASTMD570 | % | 0.03 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Specific heat Specific heat/DSC | Specific heat (50℃) | DSC | J/㎏・℃ | 1250 | - |
Specific heat (200℃) | DSC | J/㎏・℃ | 1710 | - | |
Deflection Temperature under Load Deflection Temperature under Load/ASTMD648 | Deflection temperature under load (1.8MPa, no annealing treatment) | ASTMD648 | ℃ | 276 | - |
Linear expansion coefficient (flow) Linear expansion coefficient (flow)/ASTME831 | Linear expansion coefficient (flow, -50 to 50℃) | ASTME831 | 10＾-5/℃ | 1 | - |
Thermal Conductivity Thermal Conductivity/ASTME1530 | Thermal Conductivity | ASTME1530 | W/m・℃ | 0.34 | - |
Melting point Melting point/ASTMD3418 | Melting point | ASTMD3418 | ℃ | 343 | - |
Glass transition temperature Glass transition temperature/ASTMD3418 | Glass transition temperature | ASTMD3418 | ℃ | 152 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile Yield Stress Tensile Yield Stress/ISO527-2/1A/5 | Tensile Yield Stress | ISO527-2/1A/5 | MPa | 156 | - |
Tensile strain at break Tensile strain at break/ISO527-2/1A/5 | Tensile elongation at break | ISO527-2/1A/5 | % | 1.8 | - |
Tensile elongation at break (5.0mm/min) | ASTM638 | % | 1.8 | - | |
Tensile Modulus Tensile Modulus/ISO527-2/1A/1 | Tensile Modulus | ISO527-2/1A/1 | MPa | 15500 | - |
Tensile modulus (5.0mm/min) | ASTMD638 | MPa | 13000 | - | |
Bending strength Bending strength/ISO178 | Bending strength | ISO178 | MPa | 203 | - |
Bending strength | ASTMD790 | MPa | 211 | - | |
Flexural modulus Flexural modulus/ISO178 | Flexural modulus | ISO178 | MPa | 13200 | - |
Flexural modulus | ASTMD790 | MPa | 10400 | - | |
Izod impact strength Izod impact strength/ISO180 | Izod impact strength (unnotched) | ISO180 | kJ/m＾2 | 28 | - |
Izod impact strength (notched) | ISO180 | kJ/m＾2 | 5.8 | - | |
Izod impact strength (unnotched) | ASTMD4812 | J/m | 410 | - | |
Izod impact strength (notched) | ASTMD256 | J/m | 53 | - | |
Surface hardness Surface hardness/ASTMD785 | Rockwell Hardness | ASTMD785 | M | 87 | - |
Tensile strength Tensile strength/ASTMD638 | Tensile stress (5.0mm/min) | ASTMD638 | MPa | 143 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/ASTMD955 | Mold shrinkage rate MD(3.18mm) | ASTMD955 | % | - | |
Mold shrinkage rate TD Mold shrinkage rate TD/ASTMD955 | Mold shrinkage TD (3.18mm) | ASTMD955 | % | - | |
MFR MFR/ASTMD1238 | MFR(400℃,2.16kg) | ASTMD1238 | g/10min | 2.5 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Resin temperature Resin temperature/ | Resin temperature | ℃ | - | ||
Mold Temperature Mold Temperature/ | Mold Temperature | ℃ | - | ||
Drying conditions Drying conditions/ | Drying conditions | ℃ | 149 | 4.0hr |
| Color |
|---|
Black |
| Main Applications |
|---|
Automotive, bushings, thin walled parts, wear strips |
| Key Features |
|---|
Chemical resistance, flame resistance, good dimensional stability, high heat resistance, abrasion resistance |