| Manufacturer | Solvay Specialty Polymers Japan Co., Ltd. |
| Resin Name | PEEK |
| Product Name | KetaSpire |
| ISO Material Code | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ISO1183 | Proportion | ISO1183 | 1.48 | - | |
Water absorption Water absorption/ISO62 | Water absorption | ISO62 | % | 0.027 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Deflection Temperature under Load Deflection Temperature under Load/ISO75-2 | Deflection Temperature under Load | ISO75-2 | ℃ | 321 | - |
Deflection temperature under load (1.8MPa, no annealing treatment) | ASTMD648 | ℃ | 293 | - | |
Deflection temperature under load (1.8MPa, annealed) | ASTMD648 | ℃ | 293 | - | |
Linear expansion coefficient Linear expansion coefficient/ISO11359-2 | Linear expansion coefficient (0 to 50℃) | ISO11359-2 | 10.4 | - | |
Melting point Melting point/ | Melting point | ℃ | 343 | - | |
Glass transition temperature Glass transition temperature/ISO11357-2 | Glass transition temperature | ISO11357-2 | ℃ | 147 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile breaking stress Tensile breaking stress/ISO527-2/1A | Tensile breaking stress | ISO527-2/1A | MPa | 162 | - |
Tensile strain at break Tensile strain at break/ISO527-2/1A | Tensile elongation at break | ISO527-2/1A | % | 2 | - |
Tensile elongation at break (5.0mm/min) | ASTMD638 | % | 1.9 | - | |
Tensile Modulus Tensile Modulus/ASTMD638 | Tensile modulus (5.0mm/min) | ASTMD638 | MPa | 14500 | - |
Bending strength Bending strength/ASTMD790 | Bending strength | ASTMD790 | MPa | 225 | - |
Bending strength (breaking) | ISO178 | MPa | 242 | - | |
Flexural modulus Flexural modulus/ASTMD790 | Flexural modulus | ASTMD790 | MPa | 11700 | - |
Izod impact strength Izod impact strength/ISO180 | Izod impact strength (unnotched) | ISO180 | kJ/m＾2 | 32.1 | - |
Surface hardness Surface hardness/ISO2039-2 | Rockwell Hardness | ISO2039-2 | 117 | - | |
Durometer hardness (Shore D) | ISO868 | Shore D | 78 | - | |
Tensile strength Tensile strength/ASTMD638 | Tensile stress | ASTMD638 | MPa | 155 | - |
Yield strain (fracture) Yield strain (fracture)/ISO178 | Bending strain (breakage) | ISO178 | % | 2.5 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/ISO294-4 | Mold shrinkage rate MD | ISO294-4 | % | - | |
Mold shrinkage rate TD Mold shrinkage rate TD/ISO294-4 | Mold shrinkage rate TD | ISO294-4 | % | - | |
MFR MFR/ISO1133 | MFR | ISO1133 | g/10min | 13 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Resin temperature Resin temperature/ | Resin temperature | ℃ | - | ||
Mold Temperature Mold Temperature/ | Mold Temperature | ℃ | - | ||
Drying conditions Drying conditions/ | Drying conditions | ℃ | 150 | 4.0hr |
| Color |
|---|
Black |
| Main Applications |
|---|
Aircraft, bearings, bushings, film, gears, industrial applications, sheets, tubes |
| Key Features |
|---|
Chemical resistance, fatigue resistance, flame retardancy, dimensional stability, high heat resistance, abrasion resistance |
Copyright© 2025 PlaBase. All Rights Reserved.