| Manufacturer | Solvay Specialty Polymers Japan Co., Ltd. |
| Resin Name | HPPA |
| Product Name | Kalix |
| ISO Material Code | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ | Proportion | 1.4 | - | ||
Water absorption Water absorption/ASTMD570 | Water absorption rate (23℃, 24hr) | ASTMD570 | % | 0.13 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Deflection Temperature under Load Deflection Temperature under Load/ISO75-2/B | Deflection temperature under load (0.45MPa, no annealing treatment) | ISO75-2/B | ℃ | 223 | - |
Deflection temperature under load (1.8MPa, no annealing treatment) | ISO75-2/A | ℃ | 215 | - | |
Glass transition temperature Glass transition temperature/ASTMD3418 | Glass transition temperature | ASTMD3418 | ℃ | 55 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile strain at break Tensile strain at break/ISO527-2 | Tensile strain at break | ISO527-2 | % | 3 | - |
Tensile Modulus Tensile Modulus/ISO527-2 | Tensile Modulus | ISO527-2 | MPa | 13000 | - |
Bending strength Bending strength/ISO178 | Bending stress | ISO178 | MPa | 275 | - |
Flexural modulus Flexural modulus/ISO178 | Flexural modulus | ISO178 | MPa | 11500 | - |
Izod impact strength Izod impact strength/ISO180 | Izod impact strength (unnotched) | ISO180 | kJ/m＾2 | 80 | - |
Izod impact strength (notched) | ISO180/1A | kJ/m＾2 | 20 | - | |
Tensile strength Tensile strength/ISO527-2 | Tensile stress | ISO527-2 | MPa | 175 | - |
Yield Strain Yield Strain/ISO178 | Bending strain (breakage) | ISO178 | % | 3.5 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Dielectric constant Dielectric constant/ASTMD150 | Dielectric constant (1kHz) | ASTMD150 | 3.83 | - | |
Dielectric constant (1MHz) | ASTMD150 | 3.62 | - | ||
Dielectric loss tangent Dielectric loss tangent/ASTMD150 | Dielectric tangent (1kHz) | ASTMD150 | 0.012 | - | |
Dielectric tangent (1MHz) | ASTMD150 | 0.012 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/Internal Method | Mold shrinkage rate MD | Internal Method | % | 0.15 | - |
Mold shrinkage rate TD Mold shrinkage rate TD/Internal Method | Mold shrinkage rate TD | Internal Method | % | 0.55 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Resin temperature Resin temperature/ | Resin temperature | ℃ | - | ||
Mold Temperature Mold Temperature/ | Mold Temperature | ℃ | - | ||
Drying conditions Drying conditions/ | Drying conditions | ℃ | 80 | 4.0-12hr |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Filler Content Filler Content/ | Filler content (GF) | % | 40 | - |
| Color |
|---|
White |
| Main Applications |
|---|
Mobile Phones, Electrical Components, Electrical/Electronics, Thin-walled Components |
| Key Features |
|---|
High speed molding cycle, good dimensional stability, impact resistance, good appearance, high flow, high rigidity, high strength, hot water moldability, low warping, paintable, platable |