| Manufacturer | Solvay Specialty Polymers Japan Co., Ltd. |
| Resin Name | HPPA |
| Product Name | Kalix |
| ISO Material Code | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ISO1183 | Density | ISO1183 | g/cm＾3 | 1.58 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Deflection Temperature under Load Deflection Temperature under Load/ISO75-2/B | Deflection temperature under load (0.45MPa, no annealing treatment) | ISO75-2/B | ℃ | 257 | - |
Flammability Flammability/UL94 | Flammability | UL94 | NaN | 0.35mm,Black |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile Yield Stress Tensile Yield Stress/ISO527-2 | Tensile Yield Stress | ISO527-2 | MPa | 190 | - |
Tensile strain at break Tensile strain at break/ISO527-2 | Tensile strain at break | ISO527-2 | % | 1.9 | - |
Tensile Modulus Tensile Modulus/ISO527-2 | Tensile Modulus | ISO527-2 | MPa | 17000 | - |
Bending strength Bending strength/ISO178 | Bending strain stress (3.5%) | ISO178 | MPa | 280 | - |
Flexural modulus Flexural modulus/ISO178 | Flexural modulus | ISO178 | MPa | 15000 | - |
Izod impact strength Izod impact strength/ISO180 | Izod impact strength (unnotched) | ISO180 | kJ/m＾2 | 45 | - |
Izod impact strength (notched) | ISO180/1A | kJ/m＾2 | 12 | - | |
Yield Strain Yield Strain/ISO178 | Bending strain (breakage) | ISO178 | % | 2.5 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Dielectric constant Dielectric constant/ASTMD2520 | Dielectric constant (2.40GHz) | ASTMD2520 | 4.2 | - | |
Dielectric loss tangent Dielectric loss tangent/ASTMD2520 | Dielectric loss tangent (2.40GHz) | ASTMD2520 | 0.01 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/Internal Method | Mold shrinkage rate MD | Internal Method | % | 0.12 | - |
Mold shrinkage rate TD Mold shrinkage rate TD/Internal Method | Mold shrinkage rate TD | Internal Method | % | 0.28 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Resin temperature Resin temperature/ | Resin temperature | ℃ | - | ||
Mold Temperature Mold Temperature/ | Mold Temperature | ℃ | - | ||
Drying conditions Drying conditions/ | Drying conditions | ℃ | 4.0-12hr |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Filler Content Filler Content/ | Filler content (GF) | % | 45 | - |
| Color |
|---|
Black, colored, natural color |
| Main Applications |
|---|
Mobile Phones, Electrical Components, Electrical/Electronics, Thin-walled Components |
| Key Features |
|---|
High speed molding cycle, good dimensional stability, impact resistance, good appearance, high flow, high rigidity, high strength, hot water moldability, low warping, paintable, platable |