| Manufacturer | Toray Industries, Inc. |
| Resin Name | PA610 |
| Product Name | Amilan |
| ISO Material Code | ＞PA610＜ |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ISO 1183 | Density (23℃) | ISO 1183 | g/cm^3 | 1.32 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Deflection Temperature under Load Deflection Temperature under Load/ISO-75-2/A | Deflection temperature under load (1.8MPa, no annealing) | ISO-75-2/A | ℃ | 205 | - |
Melting point Melting point/DSC method | Dissolving temperature | DSC method | ℃ | 225 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile strain at break Tensile strain at break/ISO 527-2 | Tensile strain (break point, 23℃) | ISO 527-2 | % | 4 | - |
Bending strength Bending strength/ISO 178 | Bending strength (23℃) | ISO 178 | MPa | 250 | - |
Flexural modulus Flexural modulus/ISO 178 | Flexural modulus (23℃) | ISO 178 | MPa | 8400 | - |
Charpy impact strength Charpy impact strength/ISO 179 | Charpy impact strength (notched, 23℃) | ISO 179 | kJ/m^2 | 14 | - |
Tensile strength Tensile strength/ISO 527-2 | Tensile strength (23℃) | ISO 527-2 | MPa | 160 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Filler Content Filler Content/ | Filler Content | % | 30 | GF |
| Main Applications |
|---|
Fasteners, Mechanical Parts |
| Key Features |
|---|
Standard, GF30% |