| Manufacturer | Toray Industries, Inc. |
| Resin Name | PC+PBT |
| Product Name | Toraycon |
| ISO Material Code | ＞PBT+PC-I＜ |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Density Density/ISO 1183 | Density (23℃) | ISO 1183 | g/cm^3 | 1.22 | - |
Water absorption Water absorption/ISO 62 | Water absorption, in water (24hr, 23℃) | ISO 62 | % | 0.07 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Deflection Temperature under Load Deflection Temperature under Load/ISO 75-2/B | Deflection temperature under load (0.45MPa, no annealing) | ISO 75-2/B | ℃ | 110 | - |
Deflection temperature under load (1.8MPa, no annealing) | ISO 75-2/A | ℃ | 94 | - | |
Linear expansion coefficient Linear expansion coefficient/ISO 11359-2 | Coefficient of linear thermal expansion (-30 to 100°C) | ISO 11359-2 | ×10^-5/℃ | 8 | - |
Flammability Flammability/Toray method | Flammability rating, UL 94 | Toray method | NaN | Quite |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Tensile strain at break Tensile strain at break/ISO 527-2 | Tensile strain (break point, -40℃) | ISO 527-2 | % | 37 | - |
Tensile strain (break point, 23℃) | ISO 527-2 | % | 80 | - | |
Tensile strain (break point, 80℃) | ISO 527-2 | % | 80 | - | |
Bending strength Bending strength/ISO 178 | Bending strength (-40℃) | ISO 178 | MPa | 124 | - |
Bending strength (23℃) | ISO 178 | MPa | 91 | - | |
Bending strength (80℃) | ISO 178 | MPa | 45 | - | |
Flexural modulus Flexural modulus/ISO 178 | Flexural modulus (-40℃) | ISO 178 | MPa | 2600 | - |
Flexural modulus (23℃) | ISO 178 | MPa | 2300 | - | |
Flexural modulus (80℃) | ISO 178 | MPa | 1400 | - | |
Charpy impact strength Charpy impact strength/ISO 179 | Charpy impact strength (notched, -40℃) | ISO 179 | kJ/m^2 | 15 | - |
Charpy impact strength (notched, 23℃) | ISO 179 | kJ/m^2 | 65 | - | |
Charpy impact strength (unnotched, -40) | ISO 179 | kJ/m^2 | No breaks | ||
Surface hardness Surface hardness/ISO 2039-2 | Rockwell hardness (M-scale, 23℃) | ISO 2039-2 | 51 | - | |
Tensile strength Tensile strength/ISO 527-2 | Tensile strength (-40℃) | ISO 527-2 | MPa | 86 | - |
Tensile strength (23℃) | ISO 527-2 | MPa | 61 | - | |
Tensile strength (80℃) | ISO 527-2 | MPa | 35 | - |
Blurred items can be viewed by registering or logging in.
Blurred items can be viewed by registering or logging in.
| Property | Details | Inspection Methods | Unit | Value | Note |
|---|---|---|---|---|---|
Mold shrinkage rate MD Mold shrinkage rate MD/Toray method | Mold shrinkage, parallel: 3.00mm (80×80×3mm) | Toray method | % | 0.8 | - |
Mold shrinkage rate TD Mold shrinkage rate TD/Toray method | Molding shrinkage, vertical: 3.00mm (80×80×3mm) | Toray method | % | 0.8 | - |
| Main Applications |
|---|
Automotive exterior parts, automotive applications |
| Key Features |
|---|
Unreinforced, high impact, low warpage |